浅谈首秦高炉降料面操作及设想 王效东 郭 寂 （秦皇岛首秦金属材料有限公司，秦皇岛 066326 ） 1 摘 要 首秦公司现有两座高炉，均采用喷注式薄壁炉衬、全软水密闭循环冷却设计，而采用薄壁炉衬设计的高炉 运行一段时期后，需要组织降料面重新喷涂造衬。2008 年～2009 年的两年期间，首秦公司两座高炉分别组织了两 次降料面喷涂造衬工作，本文总结了这四次降料面技术操作的实践经验，提出了对未来降料面操作优化的一些设想 和建议。 关键词 高炉 降料面 操作 Discussion on the Operation and Proposal of Shouqin Blast Furnace Lowering Charge Level Wang Xiaodong Guo Ji (Qinhuangdao Shouqin Metal Material Co.,Ltd., Qinhuangdao, 066326) Abstract At present in Shouqin company there are two Blast furnace both taking the design of spaying thin skinned lining and soft water closed circulation cooling。After the operation period of thin skinned lining in the blast furnace, the lowering charge level should be coated relining. During the years of 2008-2009,Shouqin company has implemented the lining of lowering charge level twice individually in two blast furnaces. The article summarizes the practical experience regarding the four lowering charge level operation and gives the proposal on the optimizing future operation of lowering charge level. Key words Blast furnace, lowering charge level, operation 1 引言 3 3 首秦公司现有两座高炉，其中 1 号高炉有效容积 1200m ，2 号高炉有效容积 1780 m ，分别于2004 年 6 月 6 日和2006 年 5 月 31 日开炉投产。高炉煤气除尘均采用全干法除尘工艺，炉体为全冷却壁无勾头软水密 闭循环冷却，喷注式薄壁炉衬。 由于高炉煤气除尘采用全干法除尘工艺，要求在降料面操作过程中不仅要考虑气密箱温度的控制，还要 考虑煤气温度不能超过干法除尘箱体布袋安全使用的要求，这给高炉的操作增加了相当大的困难。 2008 年～2009 年两座高炉分别进行了两次降料面喷涂造衬工作，通过精心计划、准备和严格操作，顺 利完成降料面工作并为扒料和开炉都创造了良好的条件。 2 四次降料面情况 2008 年 5 月 1 号高炉：料面处在风口下沿以下，料面圆周方向均匀平整；炉墙喷注料基本侵蚀干净， 王效东，男，本科，高级工程师，从事技术管理及指导工作。 郭寂，男，本科，工程师，从事技术管理工作。 浅谈首秦高炉降料面操作及设想 8-481 风口带上边到六段冷却壁中下部有一圈粘结物，为碳渣混合物，不是很牢固，比较容易清理。 2008 年 7 月2