鞍钢转炉AOA动态控制系统开发及应用.pdfVIP

鞍钢转炉 AOA 动态控制系统开发及应用 万雪峰 王丽娟 李德刚 廖相巍 曹 东 常桂华 康 伟 （鞍钢股份有限公司技术中心，鞍山 114009 ） 1 摘 要 本文介绍了鞍钢自主开发的转炉 AOA 动态控制系统及其应用效果，应用该系统对转炉吹炼过程及终点进 行控制，得出如下结论：(1) 原料管理是转炉自动化炼钢成败的关键因素之一，不但直接影响操作过程，而且还影 响吹炼终点效果；(2) 在±0.02%允许误差范围内，AOA 终点碳含量 w[C]一拉命中率已经达到 93.0%，补吹率仅为 1.4%；(3) 在±20%允许误差范围内，终点温度 T 一拉命中率达 92.9%；(4) 在±30×10-6 误差范围内，终点磷含量 w[P] 一拉命中率达到 83.1%。 关键词 AOA 炉气分析 转炉吹炼 动态控制 Develepment and Applying of Converter AOA Kinetic Control System in Ansteel Wan Xuefeng Wang Lijuan Li Degang Liao Xiangwei Cao Dong Chang Guihua Kang Wei (Technology Center of Ansteel Co., Ltd., Anshan, 114009) Abstract Converter AOA kinetic control system developed by Ansteel independently and its application effect were described in this article, and blowing process and end could be controlled applying this system and arriving at the following conclusions: (1) Raw material management was crucial to the success of the steelmaking automation in converter, not only the operation process was affected by it, but also the effect of blowing end was affected by it; (2) Within the scope of permissible error ±0.02%, the single-time hit rate of carbon content w[C] at the blowing end could reach 93.0% applying AOA system, the compensating blowing rate was only 1.4%; (3) Within the scope of permissible error ±20 ℃, the single-time hit rate of temepature T at the blowing end could reach 92.9%; (4) Within the scope of permissible error ±30×10-6, the single-time hit rate of phosphorus content w[P] at the blowing end could reach 83.1%. Key words AOA(Ansteel Off-gas Analysis) ， off-gas analysis ，BOF blowing ， kinetic control 鞍钢炼钢总厂一工区 100t 转炉是在老