采用铁矿石替代废钢的炼钢工艺实践.pdfVIP

采用铁矿石替代废钢的炼钢工艺实践 田志国 丁金虎 汤 伟 ， （湘潭钢铁集团公司, 湘潭 411101 ） 1 摘 要 介绍了湘潭钢铁集团公司炼钢厂80 t 转炉采用铁矿石替代部分废钢作为冷料，通过调整转炉的物料配比 和操作方式，以降低炼钢成本的工艺实践。实践证明，采用铁矿石替代废钢，可使矿石消耗量增加，而废钢消耗量 减少，从而降低钢铁料、氧气、化渣剂等成本支出。 关键词 铁矿石 废钢 炼钢 工艺实践 The Steelmaking Technology Practice about Iron Ore Serves as Alternatives to Scrap Tian Zhiguo Ding Jinhu Tang Wei (Xiangtan Iron and Steel Group Corporation, Xiangtan, 411101) Abstract This paper the 80t converter using iron ore as cold material partly take the place of scrap in Steelmaking plant of Xiangtan Iron and Steel Group Corporation was introduced. Through adjusting the converter materials rate and optimizing operation, the cost of steelmaking was reduced.It was found that , using iron ore serves as alternatives to scrap, the iron ore consumption was increased, the scrape consumption was decreased and the cost about oxygen, steel material, flux, etc .was dropped. Key words iron ore ，scrape，steelmaking，technology practice [1] 据测算，铁水、废钢、原材料、合金等的成本占炼钢总成本的70 ％以上 。根据热平衡计算可知，转炉 炼钢时炉内热量有富余，必须加入适量的冷却剂。转炉炼钢可用的冷却剂有废钢、铁矿石、氧化铁皮等，用 量最多的为废钢。2010 年以来，废钢价格暴涨，且采购困难，造成炼钢厂成本超支。湘钢在炼铁产能富余 的情况下，使用铁矿石替代废钢，以降低炼钢成本，平衡生产。 1 工艺条件 1.1 设备条件 湘钢炼钢厂现有3 座公称容量为80 t 的转炉，平均装入量为98 t ，转炉冶炼周期为32 min ，吹氧时间为 3 15 min ，供氧流量为17500～19500 Nm /h ，氧压为0.7～0.9 MPa 。炉外精炼装备含3 座CAS （Composition Adjustment by Sealed Argon Bubbling ）站、3 座LF （Ladle Furnace ）钢包炉、1 台VD （Vacuum Degassing ） 炉，连铸含2 台8 机8 流罗可普小方坯连铸机、1 台4 机4 流克虏伯型方坯连铸机、1 台4 机4 流康卡斯特 方坯连铸机。 根据工艺要求的不同，炼钢厂的工艺流程主要分为：转炉—CAS—铸机—CAS—LF— （VD ）—铸机， 田志国 (1977—)，男，湖南湘潭人，湘潭钢铁集团公