超低碳钢冶炼实践.pdfVIP

超低碳钢冶炼实践 赵艳玲 潘树敏 李太全 （河北钢铁集团 邯郸钢铁公司 邯宝钢铁公司 炼钢厂，邯郸 056015 ） 1 摘 要 邯宝公司炼钢厂通过冶炼超低碳钢实践，解决了诸如钢中硫、磷的控制、顶渣改质、超低碳控制、超低氮 控制、夹杂物控制、钢包水口自开、塞棒上涨、铸坯边部气泡和卷渣等技术难题，成功实现了多炉连浇和批量生产， 完善了超低碳钢生产过程中的关键控制技术。 关键词 转炉 硫控制 磷控制 超低碳 超低氮 顶渣改质 RH 夹杂物 板坯连铸 Ultra-low Carbon Steel Smelting Practice Zhao Yanling Pan Shumin Li Taiquan (Hanbao Corporation Steel Plant, Handan, 056015) Abstract Han bao low carbon steel smelting companys steel plant through the practice of solution of sulfur such as steel, phosphate control, the top slag modification, control of ultra-low carbon, low nitrogen control, inclusion control, ladle nozzle from the opening, plug stick up, slab edge bubble and slag and other technical problems, successful multi-furnace continuous casting and mass production, improved ultra-low carbon steel production process control technology in the key. Key words Converter, sulfur control, phosphorus control, ultra-low carbon, low nitrogen, top slag modifier, RH, inclusion, slab casting 1 引言 超低碳铝镇静钢 ，广泛用于汽车板、钢质易拉罐等产品，对钢材的表面质量和深冲成形加工性能要求 极高，要求[C]40ppm，甚至要求[C]20ppm。邯宝公司炼钢厂从2009 年 7 月开始超低碳钢的试生产，在生 产超低碳钢过程中，从工艺流程优化、RH 真空精炼技术完善、连铸工艺优化到钢包管理、过程温度控制以 及生产过程衔接与组织等多方面开展了深入细致的工作，解决了诸如钢中硫控制、钢中磷控制、顶渣改质、 超低碳控制、超低氮控制、夹杂物控制、水口自开、塞棒上涨、铸坯边部气泡和卷渣等技术难题，成功实现 了多炉连浇和批量生产，完善了超低碳钢生产过程中的关键控制技术，目前所生产的超低碳钢碳、硫、磷、 氮含量分别可以达到 0.0010%、0.007%、0.008%和 0.002%，钢中夹杂物水平比较低，铸坯内部质量硫印分 析全部在 C 类 0.5 以下，产品的实物质量达到国内同行业一流水平。 2 工艺流程选择 为了满足满足高品质超低碳钢对极低氮和极低碳含量的要求，经过充分论证，邯宝公司炼钢厂选用了脱 硫预处理→转炉→RH→CC 工艺流程， 此工艺流程二次精炼只过 RH 炉，具有较强的低成本优势。 赵艳玲(1971-)，女，工程师，大专，1995 年毕业于北京科技大学钢铁冶金专业，现在河北钢铁集团邯钢公司邯宝炼钢厂从事生产技术管理工作， LNANCY009@163.com 超低碳钢冶炼实践 8-809 3 关键工艺控制技术 3.1 钢中硫控制 通过控制冶炼过程原料的硫含量来控制终