铁基材质高炉冷却壁的解剖研究与破损机理.pdfVIP

铁基材质高炉冷却壁的解剖研究与破损机理 胡源申 张文明 岳海峰 （安徽工业大学，马鞍山 243002 ） 摘 要 对使用开路循环水、预处理循环水、软水密闭、纯水密闭四种冷却水质和循环方式，使用灰铸铁、球墨铸铁、 耐热铸铁、铸钢和铜五种材质的一代服役后高炉冷却壁进行了系统解剖研究。分析比较了不同材质冷却壁的力学性能、 导热性能、抗结垢性能、易加工性能和经济性能，揭示了铁基材质冷却壁的微观破损机理和壁内水管的成垢机制。 关键词 高炉长寿 铁基材质 冷却壁 破损机理 成垢机制1 Dissection Study on Damage Mechanism of Iron BF Cooling Stave Hu Yuanshen Zhang Wenming Yue Haifeng (Anhui University of Technology, Ma’anshan, 243002) Abstract The BF cooling stave after a campaign life made by the materials of grey cast iron, nodular cast iron, resistant cast iron，cast steel and copper and used of open loop water，pretreatment circulating water ，soft water closed circulation and pure water closed circulation have been systematically dissectional studied respectively. The comparative analysis of the mechanical property ，conducting property，scab retardation property，easy processing and the economical of different materials of cooling stave have revealed the micro damage mechanism of iron BF cooling stave and the scaling mechanism of the internal pipe. Key words BF longevity, iron based material, cooling stave, damage mechanism, scaling mechanism 1 引言 目前国内高炉冷却循环水使用按水质劣优顺序和循环方式排列有四种:即开路冷却水、预处理循环水、软水密闭和 纯水密闭循环。高炉冷却壁材质选用有灰铸铁、球墨铸铁、耐热铸铁、铸钢和纯铜五种。其中前四种均属铁基材质。 高炉冷却壁的使用寿命是制约高炉长寿的最重要因素之一。因此，搞清不同材质冷却壁服役中使用不同循环 水质的破损机理，以及壁内水管中结垢的成垢机制，对高炉长寿的系统实践，从设计到制造、建设、筑炉、烘炉、 开炉、生产、维护等各个环节都具有基础性的指导和决定作用。文献[1]-[9]反映出本课题组近些年对此已积累的认识。 2 铁基材质高炉冷却壁的性能特点 铁基材质冷却壁主要指使用 HT 、QT 和 ZG ，以及包括国内某钢使用的耐热铸铁材质制作的冷却壁。 其化学组成特点是铸体内均含碳、硅、锰、磷、硫、钒、钛等元素。其金相组成特点是铁素体加珠光体分 布。其力学性能特点是均具有较好的抗拉强度和延伸率。其导热性能特点是均具有较大的导热系数。其经 济性能特点是制作成本不是太高，因而国内外高炉的冷却壁目前使用得较多。 胡源申，男，副教授，从事高炉长寿工艺研发，huys@ahut.edu.cn 8-604 第八届（2011 ）中国钢铁年会论文集 3 铁基材质高炉冷却壁服役后解剖研究得到的力学性能特点比较