260t复吹转炉IF钢冶炼过程氮元素控制.pdfVIP

260t 复吹转炉 IF 钢冶炼过程氮元素控制 王小善 田 勇 张 越 张志文 王 鹏 温铁光 （鞍钢股份有限公司第三炼钢连轧厂，鞍山 114021 ） 摘 要 本文根据鞍钢第三炼钢连轧厂 260t 顶底复吹转炉的生产实际条件，按照 IF 钢洁净化冶炼的标准通过对现 有复吹转炉冶炼、出钢过程，以及铁水硅数、点吹时间、吹炼全程降罩等因素对钢水氮含量的影响的分析及研究， 形成了一套顶底复吹转炉钢水氮含量控制方法，使得 IF 钢出钢氮的平均质量分数控制在 11ppm，达到了洁净化冶 炼的标准。 关键词 IF 钢 控氮 复吹转炉 Controlling Methods of Nitrogen Element During If Steel Smelting Process in 260t Combined Blowing Converter Wang Xiaoshan Tian Yong Zhang Yue Zhang Zhiwen Wang Peng Wen Tieguang (No.3 Steelmaking Continuous Rolling Plant, Angang Steel Co., Ltd., Anshan, 114021) Abstract In this paper, the influence of smelting and tapping process, silicon content in hot metal, reblowing time and hood descent in whole blowing process on [N] content in tapping molten steel was investigated. Considering the practical conditions of IF steel smelting in No.3 Steelmaking Continuous Rolling Plant, Angang Steel Co. Ltd., a series of controlling methods of [N] content were proposed. The average [N] content in tapping molten steel was controlled lower than 11ppm. 1 Key words IF steel, nitrogen control, combined blowing converter 1 引言 一般情况下，氮是有害元素，主要表现在：由于 Fe N 的析出，导致钢材的时效性，降低钢的冷加工性 4 能，还造成焊接热影响区脆化。同时氮还会与钢中钛、铌、铝等元素形成氮化物夹杂，使钢的表面质量变差， 降低成材率[1] 。随着市场对汽车板的日益需求，同时对汽车板的质量也提出了更高的要求，对于汽车板氮的 控制也提出了更高的要求[2] 。 鞍钢第三炼钢连轧厂装备有公称重量为 260t 的顶底复吹转炉 3 台，采用 Küttner Trier GmbH 提供的 OTCBM 自动化炼钢控制系统。2006 年以来，针对转炉 IF 钢冶炼过程中氮的控制难点，从铁水条件、设备 状态、吹氧过程和出钢过程等角度进行了工艺分析和现场试验，并提出了一系列控制钢水氮含量的措施。 2 铁水条件对[N]含量影响分析 图 1 统计分析了正常冶炼状态下，不同铁水硅含量与终点钢水氮含量的关系。结果表明，铁水硅含量小 于 0.35%时，转炉终点钢水中平均氮含量较高，平均大于 10ppm。而铁水硅数大于0.35%时，终点钢水的氮 王小善，男，学士，助工，从事炼钢技术管理。 8-224 第八届（2011 ）中国钢铁年会论文集 含量能稳定地控制在 10ppm 以内。铁水硅含量较低时，前期渣料不易快速融化，熔渣流动性变差，吹炼过 程熔渣有返干现象，造成吹