北营1780热连轧层流冷却模型.pdfVIP

1北营 1780 热连轧层流冷却模型 尹 威 （北营钢铁集团轧钢厂，本溪 117017 ） 摘 要 热轧带钢卷取温度是决定带钢质量的重要因素。随着市场对热带钢产品要求的不断提高，北钢 1780 生产 线为了提高产品的质量，增加在市场上的竞争力，2010 年北钢 1780 热连轧生产线对层流冷却模型进行了改造。本 文讲述了改造后的层流冷却控制模型的数学公式与实际投用后的效果。经过投入后的一段测试，该模型达到了较高 的控制精度，完成了改造的目的。 关键词 热带钢轧机 卷取温度控制 数学模型 冷却 The Model of Bei Gang 1780 Hot Strip Mill Coiling Temperature Yin Wei （Beiying Iron and Steel(Group) Corporation, Benxi , 117017 ） Abstract The coiling temperature of hot rolled steel strip is a very important factor for quality of product. With the more and more heightened requirements of market,the coiling temperature model of Bei Gang 1780 hot strip mill was rebuilded in order to inprove the quality of product and increase the ability of market competition in 2010.The rebuilded mathematic formula of coiling temperature model and the results of practical application are introduced in this paper. the results indicate that the coiling temperature model achieve a higher controlling precision . Key words hot strip mill,cooling temperature control,mathematical model,cooling 1 卷取温度模型概述 卷取温度控制采用数学公式、模型表和自学习值作为基础计算并生成了层冷喷水模式，保证卷取入口温 度在很小的公差范围内。同时通过改变层冷喷水模式，结合设定程序和闭环控制程序，纠正卷取入口实测温 度与给定目标温度的偏差。另外，卷取温度控制为精轧出口温度提供了速度闭环控制功能。 模型中的公式，数学模型主要源自热传导第一定律、已出版的文献资料和历史经验方法。模型表中的一 些系数值是通过精轧目标厚度和钢种级别确定的，这样可以使卷取模型表与北台 1780mm 热连轧轧过的产 品相匹配。 关于层冷控制模型，当中最关键的数学模型是层冷辊道的带钢温降模型，该温降模型采用集中参数方法 计算带钢温降。带钢运行在层冷辊道时，其金属结构是在变化的，大多时候是从奥氏体向铁素体转变。在金 属结构转变期间，带钢的热传导特性变化范围很大。曾经有一些科学家试图建立一种数学模型来适应这种变 化，但是我们发现这种技术会给控制带来更多的噪声干扰，远远大于其带来的好处（增加了模型理解的复杂 尹威，男，本科，高级工程师，于 2006 年 7 月毕业于辽宁工程技术大学电子信息工程专业。 现从事工作：1780 二级计算机室，层流冷却模型专职负责人。 8-146 第八届（2011 ）中国钢铁年会论文集 性），结果是弊大于利。经过对热连轧带钢卷取温度控制大量的试验测试后，北台 1780 生产线采用了一种集 中参数方法。该方法建立一个简单的精轧出