表面检测系统在热轧不锈钢质量改进中的应用研究 孙静全 侯宝辉 蔡 才 （宝山钢铁股份不锈钢事业部热轧厂，上海 200431 ） 摘 要 本文主要研究不锈钢事业部热轧厂实际生产和装备情况下，表面检测系统不锈钢检验中的应用情况。基于 表面检测系统不锈钢缺陷检出率满足要求的前提下，主要针对不锈钢轧制间隙时间、检验人员查看表面检测系统缺 陷速度。同时结合表面检测系统不锈钢检测中的缺陷分类率，得出现场检验人员能保证质量的系统显示最大缺陷数。 根据实际系统显示缺陷数与现场检验人员能保证质量的系统显示最大缺陷数对比，判定钢卷是否需要质量预防。 关键词 不锈钢 表面检测 质量检验 质量改进 Application of Surface Inspection System in Quality Improvement Sun Jingquan Hou Baohui Cai Cai (Baoshan Iron Steel Co., Ltd. Stainless Steel Branch, Shanghai, 200431) Abstract The research studies surface inspection system in quality inspection application in baosteel Stainless Branch. This research is base on the real defect is inspected. The research recorded the time between two coins which are continue rolled in hot rolling mill. And also recorded the inspect defect speed of quality inspector who inspect defect in surface inspection. According the rate of classified defect , the research can get the Max inspect defect number which is quality sure .And then According the Max inspect defect number and the surface inspection system defect number which is showed, the research can get which steel should be improved .1 Key words stainless steel, surface inspection, quality inspection, quality improvement 1 引言 随着用户对质量需求的提高，尤其在不锈钢领域，由于不锈钢成品多数应用于外观件，所以热轧的下工 序往往对表面质量要求较高，导致要求不锈钢热轧产品表面要求也越来越高。对于热轧不锈钢产品而言质量 抽检已经不能满足用户的要求，要求在线质量检验人员采用全检的方式进行表面检验。基于这些要求，利用 光学相机高速成像原理的表面检测系统应运而生。从 2007 年开始国内不锈钢企业在热轧领域先后引进了该 检测装置。如宝钢、酒钢、太钢、张浦等。 宝钢不锈钢事业部在 2006 年从 Cognex 公司引进表面检测装置。作为国内首家引进表面检测系统设备 的不锈钢企业，目前已经成功的将表面检测系统应用于不锈钢表面质量检验中，成为热轧质量检验的核心工 具和核心技术。 1孙静全，男，工学学士，工程师，从事热轧质量检验，sunjingquan1980@ 表面检测系统在热轧不锈钢质量改进中的应用研究 8-341 2 应用基本条件 2.1 检验人员熟知系统缺陷图片与不锈钢实物缺陷对应关系 现场检验人员是表面检测系统的