邯钢CSP精轧机烟气抑制系统改进设计.pdfVIP

邯钢 CSP 精轧机烟气抑制系统改进设计 周英超 王会军 刘耀辉 苑 勇 卢鸿章 (河北钢铁集团邯钢公司 连铸连轧厂，邯郸 056015) 摘 要 针对热连轧烟气抑制系统除烟效果差、除烟不彻底、厂房环境差、麻点事故多等问题，通过对集管的布置 方式、喷射角度、喷嘴选型等进行了改进，并对改进喷嘴的喷射覆盖面和角度进行了试验，同时还设计了过滤装置 和二次烟气抑制系统，经过改进的热连轧烟气抑制系统可以有效地抑制轧制过程中产生的烟气，降低麻点，提升带 钢表面质量。 关键词 热连轧 烟气抑制 改进 设计 Improved Design of Fume Suppression System in Han Gang CSP Finishing Mill Zhou Yingchao Wang Huijun Liu Yaohui Yuan Yong Lu Hongzhang （Concasting and Conrolling Plant，Handan Iron and Steel Company,Handan, 056015 ） Abstract For hot continuous rolling fume suppression systems in addition to smoke effect difference and smoke removal is not complete, work environment, pitting accidents and other issues that through the set of layout, spray nozzle selection angle etc have been improved and doing the experiment of the improvement spray nozzle，s coverage and Angle， at the same time also designed the filter and secondary fume suppression systems, improved hot rolling fume suppression system can effectively inhibit the rolling process results in the flue gas, reduce pitting, improve strip surface quality. Key words hot continuous rolling, fume suppression, improvement, design 1 引言 邯钢CSP 精轧烟气抑制系统布置在精轧机F4 、F5 、F6 的出口，它的主要功能就是抑制在高速轧制时产 生的烟气，即微小的高温粉尘，避免烟气随着轧机出口的负压进入轧辊辊缝，进而附着在轧辊上，使带钢产 生麻点，从而降低轧辊的正常轧制量、增加辊耗、提高生产成本。目前，随着钢材新品种的不断开发，对带 钢的质量要求更加严格，现有的烟气抑制装置已经不能满足当前的生产现状，存在经常发生喷嘴堵塞、集管 寿命低、除烟效果差、除烟不彻底、厂房环境差等问题。鉴于以上情况，很有必要对现有的烟气抑制装置进 行改进。 2 现场调查 2.1 结构及功能位置 精轧烟气抑制系统主要由主水管路、截止阀、气路控制阀、出口上下两排集管等组成，控制阀的开启和 邯钢CSP 精轧机烟气抑制系统改进设计 关闭通过带钢跟踪系统实现自动控制，上下两排集管向带钢的上下表面喷射扇形面得高压水，抑制烟气的形 成，防止烟气扩散，见图1 图1 1—上支承辊，2—上工作辊，3—带钢，4—下工作辊，5—下支承辊，6—主水管路，7—截止阀，8—气路控制阀，9—集管 2.2 烟气抑制的影响 当轧制宽断面和新品种时，由于产生的烟气较多，目前的烟气抑制系统不能有效地抑制烟气，从而导致 烟气不能清除干净，烟气随着出口的负压进入辊缝，附着在辊面上，降低了轧辊的正常轧制量，尤其是