薄规格板材辊式淬火机装备及工艺技术开发 1 王 超 袁 国 王昭东 王黎筠 王国栋 （东北大学轧制技术及连轧自动化国家重点实验室，沈阳 110004 ） 摘 要 薄规格板材均匀化淬火装备和工艺技术开发是钢板淬火领域内的核心技术，具有重要的实用价值， 但因其板形控制技术复杂，影响因素众多，淬火过程难度极大。本文针对薄规格钢板均匀性淬火工艺技术难题， 开发了具有高冷却强度和冷却均匀性的整体狭缝式射流喷嘴，通过调节和优化设备参数和冷却水量等工艺参数 实现薄规格钢板的良好板形控制。成功开发了系列 4mm 厚度规格低合金高强度调质钢板，淬后钢板力学性能 和平直度指标优异。 关键词 薄规格 辊式淬火机 均匀性 淬火 Development of Thin Gauge Plate Roller Quenching Equipment and Quenching Technology Wang Chao Yuan Guo Wang Zhaodong Wang Lijun Wang Guodong （The State Key Lab of Rolling Automation, Northeastern University, Shenyang, 110004 ） Abstract Development of thin gauge plate uniform quenching equipment and process is key technology in plate quenching area, and has great practical value. However, because of many affecting factors in quenching process, shape control is extremely difficult. To solve this problem, integral type slot nozzle with high cooling intensity and uniformity was developed. Accompanied with optimization of device parameters and process parameters, good plate shape of thin gauge sheet was obtained. Series of 4mm plates with excellent flatness and mechanical properties were successful developed. Key words thin gauge, roller quenching machine, uniformity, quenching 1 引言 [1] 辊式淬火机是钢板热处理线的关键设备，是当前高强度板材淬火生产的首选设备型式 。2006 年以前， 国内钢铁企业的辊式淬火机装备主要依赖进口。2006 年 12 月，东北大学轧制技术及连轧自动化国家重点实 验室（RAL ）研发出首套具有国内自主知识产权的辊式淬火机装备，并相继推广到宝钢、酒钢、南钢、新钢、 涟钢等国内各大钢铁企业。表 1 为国内各钢铁企业辊式淬火机设备及参数。 应用 RAL 研发的辊式淬火机装备及工艺技术，成功实现了宽范围厚度规格（4~120mm ）钢板的均匀性 淬火。其中，4~6mm 薄规格低合金高强度板材淬火工艺对淬火过程的冷却均匀性要求极高，淬火过程的板 形控制难度很大，是公认的国际性难题。目前仅有瑞典等国外一两家企业能够实现薄规格调质钢板的批量供 基金项目：国家重点基础研究发展计划（973 计划）（2010CB630800 ）。 王超（1985−），男，博士研究生，从事钢板热处理工艺技术开发；ral