2010 全国水处理技术研讨会论文集 2010 年 09 月 一种防止铝腐蚀的环境友好型涂层 吝大亮 杨文忠 （南京工业大学理学院，南京 210009 ） CWTC-10-014 [摘要] 利用氯丙基三乙氧基硅烷和苯胺进行反应化合成了 N 苯氨基丙基三乙氧基硅烷 （NphTES ），并以其为原料，采用浸涂的方法制备了NphTES 涂层和 NphTES- TEOS 涂层。采用 动电位极化曲线、循环伏安（CV ）、电化学阻抗谱（EIS ）法对比了两种涂层在0.15M 的NaCl 溶 液中的腐蚀特性。采用接触角测试研究了两种涂层的疏水性能，采用热重分析对比了两种涂层的 热稳定性。结果证明，NphTES- TEOS 涂层的耐蚀性能优于 NphTES 涂层，而且热稳定性能有了 进一步的提高。 [关键词] N 苯氨基丙基三乙氧基硅烷；溶胶凝胶 Abstract ： N-phenylaminopropyhriethoxysilane (NphTES) were prepared by the reactions of 3-chloropropyltriethoxysilane with aniline. NphTES and TEOS were used as precursors to prepare NphTES and NphTES-TEOS coating. Properties of corrosion resistance in 0.15M NaCl were tested by potentiodynamic polarization curves, cyclic voltammetry and electrochemical impedance spectroscopy. Hydrophobicity of two coating were tested by contact angle . Thermal stability of two coating were tested by thermal gravimetric analysis. All these measurements indicate that NphTES-TEOS coating have better corrosion resistance and thermal stability than NphTES. 目前铝合金被广泛的应用在我们日常生活，航空等各个领域，但是由于铝具有很高的活 性，耐腐蚀性自然就比较弱。环境对铝的腐蚀是不可避免的，我们只有采用一些手段来保护 铝。[1]传统的方法是采用三价的铬酸或者可溶性的铬酸盐处理，使铝表面形成钝化膜，从而 达到对铝的保护目的。但是由于用铬酸和铬酸盐处理会对环境产生较大的污染。[2]还有一种 方法是用磷酸盐处理的工艺，但是磷酸盐转化处理又非常的复杂。[3] 有机硅烷化处理是近几年发展起来的一种对铝表面处理的新工艺，由于有机硅对环境不 会产生污染，因此是一种绿色的工艺。有机硅氧烷分子（Rx Si(OR)4-x ）是一个既有有机基团， 同时也含有无机基团的分子。烷氧基硅烷的水解活性是比较低的，[4]但是在酸的催化下，有 机硅氧烷分子就会发生水解反应，水解之后能够在有机和无机界面产生交联作用。在空气中 铝合金的表面会很容易形成一层氧化膜，因此在铝的表面是含有大量的 OH-基团，水解后的 - [5] 有机硅氧烷会和铝表面的 OH 生成 Si-O-Al， 使铝基体和外边的介质隔绝，从而达到对铝的 保护目的。 N 苯氨基丙基三乙氧基硅烷（NphTES ）是一种具有很好耐高温性能的硅烷偶联剂，目 前被广泛的应用于层压板的玻璃纤维处理剂、橡胶树脂填充物的处理剂等各个方面，[6]但是 · 122 · 天津 2010 全国水处理技术研讨会论文集 却没有人研究过 N 苯氨基丙基三乙氧基硅烷在涂层防腐方面的性能。 1 试验部分 1.1 N 苯氨基丙基三乙氧基硅烷的合成 在