【毕业论文设计】45钢高频淬火工艺及性能的研究.docVIP

45钢高频淬火工艺及性能的研究 摘 要 本文研究了感应加热表面淬火对于45钢组织性能的影响，采用感应加热表面淬火技术对45钢进行表面强化，通过调整加热时间及感应电流等工艺参数，对所获得试件的淬硬层进行显微硬度测试，利用金相显微镜对试件淬硬层的组织、厚度进行研究分析。同时与正火并调质件进行硬度、金相组织等方面的比较。结果表明经过高频感应加热淬火后45钢的表面性能明显改善，表面为淬火马氏体，而心部仍为正火组织，使得试件既耐磨又有很强的韧性，所得的工艺参数将被作为生产实践的参考依据。 关键词： 45钢 高频感应淬火 硬度 Abstract The effect on the 45 steel performance after the Induction Quenching is studied .we use the Induction Quenching technology to make surface hardening on 45 steel .We adjust Process Parameters such as heating time and induced current and make the Hardened layer hardness test to the specimen that we get .Then we do the micro-hardness test, later on embed specimen and make the sample of the specimen .After that we analysis the thickness of Hardened layer on the micro-structural Microscope .For the other group of specimen , In order to obtain similar data with the first group ,we do quenching test of the specimen for measuring microstructure .The results showed that the 45 steel is improved after Induction Quenching . And the process parameters we got will be as a reference for production practice in the future. Key words： 45 steel High frequency induction quenching hardness 目 录 摘 要 I Abstract II 第1章 绪 论 - 1 - 1.1 感应加热淬火工艺概述 - 1 - 1.2 感应加热淬火技术的优点与不足 - 1 - 1.3感应加热淬火技术的应用 - 2 - 1.4 感应加热淬火技术的发展方向 - 3 - 1.4.1 感应加热淬火技术的发展 - 3 - 1.4.2 新型感应加热淬火技术 - 3 - 1.5 感应加热淬火技术常见质量问题及产生原因 - 5 - 1.6 45钢感应加热淬火技术的应用与研究 - 6 - 第2章 工艺方案制定与实验过程 - 8 - 2.1 总体实验步骤 - 8 - 2.2 实验材料与设备的选取 - 8 - 2.2.1实验材料的选取 - 8 - 2.2.2 实验设备的选取 - 8 - 2.3 实验参数与方案的确定 - 10 - 2.3.1 正火预处理参数与方案的确定 - 11 - 2.3.2 高频感应加热淬火处理参数与方案的确定 - 11 - 2.3.3 调质处理参数与方案的确定 - 11 - 2.4实验操作过程 - 12 - 2.4.1 试件的正火预处理 - 12 - 2.4.2 试件的高频感应加热淬火处理 - 12 - 2.4.3 试件的调质处理 - 12 - 第3章 实验结果分析 - 13 - 3.1 试件经高频感应加热淬火后硬度的分析比较分析 - 13 - 3.1.1相同感应电流下淬火硬度的比较分析 - 13 - 3.1.2 相同加热时间下淬火硬度的比较分析 - 15 - 3.1.3 试件回火后和回火前硬度的比较分析 - 16 - 3.2试件高频感应淬火回火与调质硬度的比较分析 - 17 - 3.3 金相组织的比较分析 - 18 - 3.3.1 试件感应加热实验前、后表面特征 - 18 - 3.3.2 试件感应加热实验前、后金相组织 - 19 - 结 论 - 21 - 致 谢 - 22 - 参考文献 - 23 - 第1章 绪