·26 · 材料导报网刊 2011 年 6 月第 6 卷第 2 期 纤维对水泥基复合材料阻裂性能的影响 邱书伟，牛春花 （巴音郭楞职业技术学院，库尔勒 841000 ） 摘要 综述了目前国内外纤维对水泥基复合材料阻裂性能的研究进展, 介绍了天然纤维、合成纤维、金属纤维、混杂 纤维等对混凝土早期塑性收缩、干缩、温缩以及有害离子的侵入等引起的收缩的阻裂作用，讨论了阻裂性能和反应机理之间 的关系，并指出了当前存在的问题及未来的研究重点和发展方向。 关键词 纤维 水泥基复合材 阻裂性 作用机理 Effects on Crack Resistance of Fiber Reinforced Cementitious Composite QIU Shuwei1, NIU Chunhua (Bayingolin College Of Vocational and Technical, Kuerle 841000) Abstract The progress in this field at home and abroad were reviewed mainly from crack resistance of fiber reinforced cementitious composite, such as natural fiber, synthetic fiber, metal fiber, hybrid fiber. The study investigated the effects of early plastic shrinkage 、drying shrinkage 、temperature reduction and the intrusion of harmful ions crack resistance of fiber reinforced cementitious composite. The relationship between the reaction mechanism and crack resistance performance was discussed. The current problems, the research emphasis and the future development direction were also mentioned. Key words fiber, cement based composite materials, crack resistance, acting mechanism [2—4] 开裂存在于水泥基复合材料的未硬化的塑性阶段、硬化 等 国外研究者提出对NFRC 进行改性以提高NFRC 的阻 阶段，同时因周围环境温度与湿度的变化，有害离子的侵入 裂性能，方法主要有两种：其一是在纤维表面使用涂料或对 等也极易生成大量裂缝，添加纤维是控制水泥基复合材料裂 NFRC 表面进行处理，增加NFRC 抗水吸收和环境引起的损 [1—3] 缝的形成和扩展的最有效地方法之一 。人们研究的纤维 害的多功能作用；其二是针对纤维活性较低的特点，通过提 从早期的天然纤维、钢纤维到近期的各种合成纤维，尤其是 高火山灰或矿渣掺量，或者通过聚合物改性水泥系统对水泥 高性能增强