螺噁嗪光致变色微胶囊的制备及防伪油墨配制.pdfVIP

·36 · 材料导报网刊 2011 年 6 月第 6 卷第 2 期 * 螺噁嗪光致变色微胶囊的制备及防伪油墨配制 蒋淑恋 (漳州市产品质量检验所，漳州363000) 摘要 以螺噁嗪为芯材，用原位聚合法制备了蜜胺脂为壁材的光致变色微胶囊。对微胶囊制备过程中的影响因素，如 预聚体的制备条件、芯壁比、表面活性剂的用量、反应各阶段的搅拌速度及反应温度等条件进行了探讨。制备出的微胶囊囊 壁光滑、粒径均匀，并配制了防伪油墨。 关键词 螺噁嗪 光致变色 微胶囊 防伪油墨 中图分类号: TB 34 文献标识码:A Preparation of Spirooxazine Photochromic Microcapsules and Its Security Ink JIANG Shulian (Zhangzhou Products Quality Supervision Institute, Zhangzhou 363000) Abstract The photochromic microcapsules with melamine resin as wall material and spirooxazine as core material were prepared by situ polymerization. The factors in the process of microcapsules prepared were discussed,for example,the conditions of preparation for the prepolymer, the core shell ratio, the amount of surfactant, the Stirring speed in mixing stages and reaction temperature and so on. The microcapsules prepared have smooth shell, uniform size, as well as the security ink have been prepared. Key words spirooxazine, photochromic, microcapsules, security ink [1] 螺噁嗪类 光致变色化合物比螺吡喃热稳定性高、抗 拌条件下，加热至 70 ℃，反应 1h，得到透明的三聚氰胺- 疲劳性强。螺噁嗪作为一种新型的有机功能材料，在变色涂 甲醛预聚物溶液。 [2] [3] 料 和防伪油墨 等方面有着非常重要的应用价值，已经引 1.3 光致变色微胶囊的制备 起了人们广泛的研究兴趣。但由于其易受温度、阳光、酸碱 取 0.12g 光致变色材料螺噁嗪加入 10mL 四氯乙烯溶 或空气等环境因素的影响而失去变色能力。若将其微胶囊化 液，配制一定浓度和体积的 SDS 水溶液(约0.7186gSDS 溶 [4—7]免受外部环境的影响，就会延长其使用寿命。本实验利 于0.65mL 去离子水)加入上述溶液中，加入13mL 的去离