毕业论文：240kA预焙铝电解槽角部伸腿肥大的预防和控制.doc

本科毕业论文 论文题目： 240kA预焙铝电解槽角部伸腿肥大的预防和控制 摘 要 本文结合实际生产对电解槽阴极伸腿肥大的原因进行了全面分析，阐述了伸腿过大对电解生产带来的诸如：槽电压偏高、直流电耗高、电流效率下降等影响，并对电解槽阴极伸腿肥大的控制措施进行了归纳和总结。 关键词：铝电解；电解槽；阴极伸腿；预防控制措施 Abstract This paper based on the actual production to gave us a comprehensive and detailed analysis for the reason of catholic leg hypertrophy of electrolytic cell, expounding the influences of excessive spread to electrolytic production, such as high voltage, high direct current power consumption, the current efficiency decline and so on, on the other hand it summarized the control measures to catholic leg hypertrophy of electrolytic cell. Key words: Aluminum electrolytic cell cathode leg control measures 目 录 TOC \o 1-3 \h \z \u HYPERLINK \l _Toc299997083 摘 要 PAGEREF _Toc299997083 \h 4 HYPERLINK \l _Toc299997084 Abstract PAGEREF _Toc299997084 \h 4 HYPERLINK \l _Toc299997085 前 言 PAGEREF _Toc299997085 \h 6 HYPERLINK \l _Toc299997086 1 青海桥头铝电有限公司240kA铝电解槽现状剖析 PAGEREF _Toc299997086 \h 7 HYPERLINK \l _Toc299997087 1.1 公司生产概况 PAGEREF _Toc299997087 \h 7 HYPERLINK \l _Toc299997088 1.1.1 公司简介 PAGEREF _Toc299997088 \h 7 HYPERLINK \l _Toc299997089 1.1.2 电解铝分公司简介 PAGEREF _Toc299997089 \h 8 HYPERLINK \l _Toc299997090 1.1.3 公司目前铝电解生产状况 PAGEREF _Toc299997090 \h 9 HYPERLINK \l _Toc299997091 2 阴极伸腿肥大的原因分析 PAGEREF _Toc299997091 \h 11 HYPERLINK \l _Toc299997092 2.1 由于电解槽存在磁场、温度场、气体流动场 PAGEREF _Toc299997092 \h 11 HYPERLINK \l _Toc299997093 2.2 由于技术参数的不匹配造成伸腿的肥大 PAGEREF _Toc299997093 \h 11 HYPERLINK \l _Toc299997094 2.2.1 氧化铝的不完全溶解造成沉淀 PAGEREF _Toc299997094 \h 11 HYPERLINK \l _Toc299997095 2.2.2 电压和铝水平不合适造成角部长伸腿 PAGEREF _Toc299997095 \h 11 HYPERLINK \l _Toc299997096 2.2.3 分子比和电解温度不合适 PAGEREF _Toc299997096 \h 11 HYPERLINK \l _Toc299997097 2.2.4 由于操作质量引起的 PAGEREF _Toc299997097 \h 12 HYPERLINK \l _Toc299997098 2.2.5 日常巡检不到位 PAGEREF _Toc299997098 \h 12 HYPERLINK \l _Toc299997099 2.2.6 设定电压下放过快，其他相应参数未跟上 PAGEREF _Toc299997099 \h 12 HYPERLINK \l _Toc299997100 3 在生产中采取的措施