化学灌浆材料在混凝土输水管论修补中的应用探讨.docVIP

化学灌浆材料在混凝土输水管修补中的应用探讨 （1金华市职业技术学院，浙江金华 2金华市质量技术监督检测院，浙江金华 ） 【摘要】混凝土输水管在制作、搬运、安装及使用等环节中出现的质量缺陷，必须经修补后才能进入到下一环节，修补成了一项不可或缺的工作。文章对混凝土输水管常见缺陷进行了分析，提出了采用化学灌浆材料进行修补的方法，并对化学灌浆材料的常见品种、施工特性、使用方法等进行了阐述。 【关键词】混凝土输水管 化学灌浆材料 Chemical grouting material in concrete application delivery pipe repair are discussed Hu zhe An 1 WangXueWu 2 (1 jinhua city, zhejiang jinhua professional technology institute 321017; 2 jinhua city quality and technology supervision inspection institute, zhejiang jinhua 321001) 【Abstract 】 in production and delivery of concrete handling, installation and use of quality defects appears in the link, must be approved by the repair to enter to the next link, repair become a indispensable work. This paper delivery common defects of concrete, the paper analyzes the chemical grouting material repair by the method of chemical grouting material, and the common breed, construction characteristics, use method were discussed. 【 keywords 】 concrete chemical grouting material delivery 1802年法国工程师Charles Bérigny 成功地利用灌浆技术将粘土浆压入地层，此后粘土灌浆、水泥灌浆一直占据着主导地位。直到1887年Jezio rsky 发明了化学灌浆（Chemical Grouting）,化学灌浆才发展起来[1]。尤其20世纪是60 年代以来，有机高分子化学浆材得到迅速的发展，各国大力发展和研制化学灌浆材料及其灌浆技术。但是自从1974 年日本福冈发生丙烯酰胺灌浆引起环境污染造成中毒事故后，化学灌浆材料及其技术的研究和应用曾一度跌入低潮，日本禁止水玻璃之外的所有其他化学浆液的应用，世界各国也禁止使用毒性较大的化学浆材[2，3，4]。20 世纪80年代，由于化学浆材的改性，化学灌浆技术又得到继续发展。化学灌浆对于细而深裂缝具有极为重要的技术价值,它可以较好地达到恢复结构整体性、耐久性及防水性的目的，现已成为混凝土结构渗漏水修补的重要手段之一[5]。本文着重就混凝土输水管修补中所使用化学灌浆材料的常见品种、主要性能指标、使用方法等进行介绍，并对实际操作过程中的注意事项给予分析，供混凝土输水管的质量缺陷修补参考。 2 混凝土输水管质量缺陷与修补方法 2.1 混凝土输水管质量缺陷分析 目前，国内混凝土输水管的品种主要有：自应力管、预应力管（一阶段、三阶段）、PCCP管。不同品种的管材，由于其在原材料、生产工艺、产品结构等方面存在差异，管材在外观检测、内水压检验及通水运行中可能出现的质量缺陷也不尽相同。即使是同一品种的管材出现了同一质量缺陷，其形成的原因也不尽相同，因此在实际生产中，应根据具体情况作具体分析。笔者根据多年在混凝土管厂的实践经验，将混凝土输水管在制作过程中出现的常见缺陷及产生的主要原因分析如下： 2.1.1 蜂窝、粘皮、麻面 产生蜂窝的的直接原因是缺陷部位由于缺少料浆而引起，此现象大多集中在承插式离心工艺管材上的承口部位以及采用震动挤压成型的一阶段管拐脖部位。 出现粘皮的主要原因是混凝土脱模强度低、钢模内壁清理不干净，造成管体表面小部分混凝土容易与模具内表面粘连。麻面则更多是由于管模过热以及拌合料未及时成型所致。 2.1.2 保护层脱落 三阶段管保护层是在管芯缠丝后再进行喷浆制作，其整体性相对于自应力管和一阶段管来说要差些，容易出现保护层脱落现象。主要