本科论文--以异辛醇和邻苯二甲酸酐(苯酐)为原料,合成增塑剂邻苯二甲酸二辛酯 (DOP)的方法.doc

摘要 本课题介绍了以异辛醇和邻苯二甲酸酐(苯酐)为原料,合成增塑剂邻苯二甲酸二辛酯 (DOP)的方法,分别以氧化锌、浓硫酸和复配型催化剂(氧化铝与辛酸亚锡以1∶1比例复配)催化合成DOP,考察催化剂对合成DOP的影响,结果表明, 氧化铝与辛酸亚锡以1∶1比例复配催化剂为最佳催化剂。考察了各反应条件对合成DOP的影响,结果表明,在异辛醇与苯酐摩尔比3∶1,氧化铝/辛酸亚锡复配催化剂用量分别占反应物总量的 0.2%时,反应时间为2.5h的反应条件下,反应物转化率达到最高95.97%。 关键词 邻苯二甲酸二辛酯 增塑剂 催化剂 ABSTRACT This subject ethylhexanol and phthalic anhydride (phthalic anhydride) as raw materials, synthetic plasticizers o-dioctyl phthalate (DOP) method, zinc oxide, two kinds of concentrated sulfuric acid monomer catalyst DOP, study tours catalyst synthesis DOP to a certain percentage of a mutual complex compound catalyst synthesis results show that aluminum oxide and stannous octoate catalyst compound in a 1:1 ratio is the best catalyst. Investigated the impact of process of conditions for synthesis of DOP results show that ethylhexanol and phthalic anhydride molar ratio 3:1, alumina / Sn compound the amount of catalyst, respectively, accounted for 0.2% of the total amount of reactants, reaction time was 2.5h process conditions, the reaction conversion rate of the highest. Key words: o-dioctyl phthalate plasticizer catalyst 目录 邻苯二甲酸二辛酯概述 5 1.1简介 5 1.2应用范围 6 1.3国内外生产工艺简介 7 1.3.1间歇法生产DOP工艺 7 1.3.2连续法生产DOP工艺 7 1.3.3酸催化工艺 8 1.3.4非酸化工艺 8 1.4我国DOP的生产能力 9 1.5 DOP的市场需求 9 1.6 DOP的催化剂技术生产的关键是催化剂 9 1.7产品现行质量标准和内控标准 9 第二章 邻苯二甲酸二辛酯的合成 11 2.1实验原料及规格 11 2.2实验仪器 11 2.3实验原理 12 2.4实验装置图 12 2.5实验步骤 12 2.5.1合成 12 2.5.2分离 13 2.5.3精制 13 2.6检测方法 13 2.6.1外观的测定 13 2.6.2折光率的测定 13 2.7数据处理 13 第三章 结果与讨论 14 3.1不同催化剂对转化率的影响 14 3.2催化剂用量对转化率的影响 14 3.3醇酐摩尔比对转化率的影响 15 第四章 结束语 16 参考文献 17 致谢 18 第一章 邻苯二甲酸二辛酯概述 1.1简介 产品名称：邻苯二甲酸二辛酯 学名：邻苯二甲酸-2-乙基己酯 别名：绝缘级二辛酯 英文名称：Dioctyl phthalate 英文别名Bis(2-ethylhexyl) phthalate; Di-2-ethylhexyl phthalate 英文简称：DOP 分子式： 结构式： 分子量：390.62 性质: DOP化学名为邻苯二甲酸二辛酯388，无色油状液体，比重0.9861(20/20 ),熔点-55℃沸点370℃（常压），不溶于水，。主要用作聚氯乙稀辅助增塑剂，相比较DOP而言，易迁徙，常与DOP结合使用，以降低增塑剂的添加成本。 沸点 370℃（1.0325×10Pa,760mmHg） 折光率 1.4859（20℃） 闪点 218.33℃（开