定向钻穿越3PE 防腐层碳纤维复合材料防护技术.docVIP

2013 年 1 月　第 32 卷 第 1 期  实验研究  文章编号：1000-8241（2013）01-0047-04 定向钻穿越 3PE 防腐层碳纤维复合材料防护技术 冯少广1　李荣光1　王文荣2　任文静3　张鑫1　李睿1　赵云峰1　赵国星1 1. 中国石油管道科技研究中心 · 中国石油天然气集团公司油气储运重点实验室，河北廊坊 065000； 2. 中国石油天然气管道局北戴河培训中心，河北秦皇岛 066100；3. 中国石油大学（北京），北京 102249 摘要：尝试通过在 3PE防腐层表面涂刷自制的聚乙烯粘接增强剂实现碳纤维/环氧树脂基复合防护 层与聚乙烯层的有效粘接。实验结果表明：在 3PE防腐层外涂刷聚乙烯粘接增强剂，可以有效改善 环氧树脂与聚乙烯层的粘接性，环氧树脂对聚乙烯的室温剪切强度由 1.73 MPa增至 3.02 MPa，剥 离强度由 2.4 N/cm增至 100.6 N/cm。通过弯曲、冲击和耐划伤实验，测试了整个防护体系的性能， 结果表明：该复合材料与聚乙烯层间形成有效粘接，且具有良好的柔韧性和抗冲击性能，可以承受 130 kg载荷的耐划伤测试。（图 6，参 10） 关键词：水平定向钻；穿越；埋地管道；外防腐层；碳纤维复合材料；防护 中图分类号：TE988　　 　　　文献标识码：A　　　　　doi：10.6047/j.issn.1000-8241.2013.01.011 3PE carbon fiber composite material protection technology in directional drilling project Feng Shaoguang1, Li Rongguang1, Wang Wenrong2, Ren Wenjing3, Zhang Xin1, Li Rui1, Zhao Yunfeng1, Zhao Guoxing1 1. CNPC Key Laboratory of Oil Gas Storage and Transportation, PetroChina Pipeline R D Center, Langfang, Hebei, 065000; 2. Beidaihe Training Center of China Petroleum Pipeline Bureau, Qinhuangdao, Heibei, 066100; 3. China University of Retroleum (Beijing), Beijing, 102249 Abstract:Effective bonding between carbon fiber/epoxy resin matrix composite protection layer and polyethylene layer is achieved with self-made polyethylene adhesive enhancer brushed on the 3PE layer. Experimental results show that the polyethylene adhesive enhancer brushed on the 3PE layer can effectively improve bonding condition between epoxy resin and polyethylene layer, and the room temperature shear strength of epoxy resin on the polyethylene layer increases from 1.73 MPa to 3.02 MPa and peel strength improves from 2.4 N/cm to 100.6 N/cm. Performance of the whole protection system is tested through bending, impact and scratch resistance tests. The results indicate that effective bonding forms between the composite material and polyethylene layer with good flexibility and impact resistance and can bear a scratch resistance test up to a 130-kg load. (6 Figures, 10 References) Key words: horizonta