28R91.高Nb管线钢静态再结晶行为的研究-RAL董毅.pdf

2007 年全国塑性加工理论与新技术学术研讨会 2007 年5 月 沈阳 高Nb 管线钢静态再结晶行为的研究* 董 毅, 肖宝亮, 许云波, 刘振宇, 王国栋 （东北大学轧制技术及连轧自动化国家重点实验室，辽宁 沈阳 110004 ） 摘 要：基于热模拟双道次压缩实验，研究了高铌HTP合金钢奥氏体区变形后道次间隔时间内的软化行为，分析了 变形温度与间隔时间对静态软化行为的影响，得出实验钢的静态再结晶激活能为338.092kJ/mol，并建立了静态再结 晶动力学模型。 关键词：静态再结晶；软化行为；激活能 Study on Static Recrystallization Behavior of Nb-microalloyed Steel DONG Yi,XIAO Baoliang, XU Yunbo, LIU Zhenyu, WANG Guodong (The State Key Lab of Rolling and Automation, Northeastern University, Shenyang 110004,China) Abstract ：The softening behavior of deformed austenite of Nb-microalloyed steel within interval of passes was studied using double-pass compression method, and the influence of temperature and interval time was analyzed. The static recrystallization activation energy of tested steel was determined to be about 338.092kJ/mol, and the static recrystallization dynamics model could be described by the following equation. KeyWords ：static recrystallization；softening behavior；activation energy 1 引言 铌是管线钢中不可缺少的重要合金元素，它能够延缓奥氏体再结晶的发生，在控轧过程中阻止 晶粒长大，并在控轧过程中，形成 Nb(C,N)沉淀，通过沉淀强化来提高钢的强度[1~3] 。传统意义的 X70 管线钢需要加入Nb 、V 、Ti 和Mo 等合金元素，但这样在提高强度的同时也增加了成本。本文 从经济角度考虑，在成分设计过程中增加价格较低的合金元素Nb 的含量而省去昂贵的Mo 和V ，再 结合高温轧制工艺(HTP)，得到性能满足传统X70 标准的高铌HTP 管线钢。 本文利用双道次压缩方法，研究高铌 HTP 钢变形间隔内奥氏体的软化行为， 为制定合理的再 结晶和未再结晶控制轧制工艺提供实验和理论依据，并且对奥氏体静态再结晶数学模型进行了探讨。 2 实验方案 2.1 实验设备和材料 本实验在Gleeble-2000热模拟实验机上进行，采用双道次压缩实验，测试真应力-真应变曲线。 将热轧后板材加工成φ8mm×15mm的圆柱形试样，实验钢主要化学成分见表1。 表1 实验钢化学成分 Table 1 Chemical composition of tested steel C Si Mn Nb Ti Al Cu Ni 0.024 0.169 1.49 0.099 0.011 0.027 0.26 0.154 2.2 实验方法 将试样以20 ℃/s 的速度加热到1200℃，保温3 分钟后以10℃/s 的速度冷却到不同温度保温30s *基金项目：国家自然科学基金项目, 项目编号