阻燃输送带骨架材料生产工艺的输送带The Study on the Technology in Producing Framework Materials for Flame Retardant Conveyor Belt HU Fengxia1 , DU Zhaofang1, ZHU Zehe2 , ZHANG Jian3 （1. College of Light-Textile Engineering and Art, Anhui Agricultural University, Hefei 230036, China；2.Wuhu Huaye industrial Fabric Co. Ltd., Wuhu 241008, China；3.Anhui Entry-Exit Inspection and Quarantine Bureau, Hefei 230061, China） Abstract: This project uses the polyester wire as warp and nylon as weft to produce the framework material for canvas conveyor belts. Direct twisting and weaving with hopsack organization are adopted in the production process. At the same time, dipping solution with flame retardancy with a synergistic effect of solvent system, adhesion system and fire resistance system has been devised to optimize the process parameters in dipping technology. The conveyor belts thus produced are with greater strength and fire resistance, which has satisfied the requirements to use them in special domains. Keywords: conveyor belt; framework materials; fire retardant dipping system; gallery organization; optimalization 1．前言 近年来，随着工业和技术的发展，作为现代散状物料连续运输的主要设备——输送带已广泛应用于冶金、化工、矿山、电站和港口等工业领域。传统的输送带大都采用棉帆布或涤棉帆布作为骨架材料，由于存在强度低、质量大、使用寿命短，与橡胶粘合强力不高等缺点，所以输送带骨架材料正向复合材料方向发展，如EP帆布、NN帆布整体带芯等[1]1000/3 D），它模量高、结晶度高、取向度高、高温下尺寸稳定；纬向选用强力高、耐热性好、伸长小的尼龙纤维（1260/2 D），生产的阻燃EP浸胶帆布能更好的满足现代工业用输送带的要求。 作者简介：胡凤霞 （1970-），女，安徽农业大学轻纺工程与艺术学院，副教授，硕士研究生，主要从事纺织新材料、新工艺和产业用纺织品的研究开发。邮编：230036 2.2主要生产设备 CableCorderCC3捻线机、SHGA21C整经OptiMax剑杆织机、德国ZELL公司浸胶机 2.3性能测试仪器 AGS-D型强力机、MK-V型热收缩仪、分析天平等 3．主要工艺技术措施 为了制造出性能优良的阻燃输送带骨架材料，本研究选用的工艺路线如下：涤纶工业长丝→CableCorderCC3加捻SHGA21C整经G177穿经筘OptiMax织造非对称捻度抱合的40m/ min， 捻度400T/m，卷绕交叉角25°。 3.2织布工艺 采用新型剑杆织机OptiMax进行织造，其无导引自由飞行剑杆系统，能实现高速高产，并最大限度降低对纱的损伤。骨架材料采用席纹结构形式织造，即用两根以上的纱线进行织造，增加了织物紧密度，有效提高了尺寸稳定性和断裂强度[2]。织造工艺参数配置如表1所示。 表1 织造工艺配置 产品 规格及工艺参数 EP阻燃输送带骨架材料 3.3浸胶工艺 3.3.1浸胶液配方 浸胶液的选配是浸胶工艺的基础。阻燃型浸胶帆布只是一个起骨架作用的半成品,它还需要与贴胶、覆盖胶组合为一体[3]。为此,本项目研制的溶剂型阻燃浸胶液由溶剂体系、粘合体系和阻燃体系组成，分别包括混合溶剂及底胶组分、