前处理对电磁屏蔽纺织品残留芳香胺检测的影响.pdfVIP

染整技术 应用技术 Dyeing Finishing Technology 前处理对电磁屏蔽纺织品残留芳香胺 检测的影响 The Influence of Pretreatment on the Determination of Residual Aromatic Amines in Electromagnetic Shielding Textiles 文 | 巫莹柱 程韵瑶 狄剑锋 张开庆 张晓利 杜文琴 为准备检测电磁屏蔽纺织品中芳香胺残留量，进一步明确旋转蒸发仪的浓缩压强、柠檬 酸盐缓冲溶液的pH值以及水浴锅振摇与否 3 个前处理参数并进行优化。实验结果表 明，旋转蒸发仪的压强为300 mbar时各类芳香胺的回收率及实验效率最高，在水浴振摇及柠 檬酸盐缓冲溶液pH值为5.5 ～ 6.1的条件下处理样品得到的检测结果更理想。 In order to determine the residual aromatic compounds in electromagnetic shielding textiles, the followed pretreatment parameters should be clear and optimized: the pressure of rotary vacuum ， evaporator water-bath vibration shake and the pH value of buffer solution. It is found that, when the pressure of rotary vacuum evaporator is 300 mbar, highest recovery of the aromatic amines and experiment efficiency will be gained. The investigation also points out that with water- bath vibration shaking and the pH value of buffer solution between 5.5 and 6.1 , relatively ideal detection results can be got. 电磁屏蔽材料分为金属材料、碳系材料和导电高分子 芳香胺的毒性研究最早起源于偶氮染料 （AZO）致癌 材料。其中导电高分子材料由于重量轻、易大面积涂敷、施 机理的研究，现在其致癌机理比较清楚（图1）。 工方便，成为一种非常理想的替代传统金属的新型电磁屏 H + － 蔽材料。导电高分子有聚乙炔、聚吡咯、聚噻吩、聚苯胺等， Ar －N=N －Ar Ar －NH2 Ar －NH+[DNA] Ar －N －[DNA] 聚苯胺性能稳定，导电性好，电磁屏蔽效果最好，但是单一 图 1 偶氮染料裂解出芳香胺及其致癌机理 聚苯胺加工性较差, 若与其他高聚物、金属复合，实现优势 毒性芳香胺 （表 1）分子量较小，较易穿透细胞膜进入 互补，改善其加工成型性。将聚苯胺粉末、金属粉末加入到 细胞核，变成活泼的亲电阳离子，与DNA中的亲核部位相互 聚丙烯酸树脂中，在有机溶剂里研磨成涂料，涂覆到织物或 吸引，发生交联反应，使正常的遗传密码发生变异，或者芳 者其他板材上。 香胺分子的扁平部位易插入DNA螺旋体的碱基对之