人工砂高性能混凝土配制技术研究分析论文.docVIP

人工砂高性能混凝土配制技术研究 宋少民 （北京建筑工程学院土木工程系） 【摘要】 本文通过试验分析不同粒径，不同材质的人工砂的基本材性，采用现代混凝土配合比设计理念，研究了人工砂高性能混凝土配合比的设计原则。通过分析粉煤灰、石粉含量对人工砂高性能混凝土在工作性和力学性能上的影响，确定粉煤灰的最佳掺量和石粉含量的范围；通过对人工砂和天然砂高性能混凝土性能的对比试验，结果表明人工砂完全可以替代天然砂配制高性能混凝土。 【关键词】 人工砂 高性能混凝土 配合比 石粉 The compound technology study of high performance concrete used artificial sand SONG Shaomin (Beijing Institute of Civil Engineering and Architecture) Abstract：Through testing research, the elementary properties of different particles and different quality of sand are analysed,with the new concept ,The concrete mix proportion design is studied. By analysing the effect of fly-ash and stone powder content on workability and mechanical performance in HPC, we find it existing optimum fly-ash and stone powder content. Through comparing artificial sand and natural sand HPC on workability, mechanical performance, The results shows that it is practicable to prepare HPC with manufactured sand, and artificial sand can replace natural sand absolutely. Key words：artificial sand；high performance concrete；mix proportion；stone powder 1 引 言 随着经济建设的飞速发展，带来了土木建筑业的空前活跃, 道路、桥梁、铁路、机场、水工建筑、近岸结构、城市建设、通讯等基础设施的建设，使得建筑材料在质和量上都达到了历史上的最高水平，消耗了大量的资源。其中占混凝土体积70%以上的砂石骨料要开山采矿，挖掘河床，每年建筑用砂石约为30多亿吨，以北京市为例，每年建设用砂石就要6400万吨，其中，仅用于商品混凝土的中、粗砂2001年使用了1066万吨，2002年为1400万吨，生态环境。随着混凝土技术的迅速发展,特别是高强度等级和高性能混凝土对骨料的要求很严,能满足其要求的天然砂数量越来越少。由于砂资源短缺,价格上涨,在经济利益的驱使下,在我国很多地区都出现了滥采乱挖天然砂的情况,特别在前几年,毁田挖砂、破坏河道挖砂的情况比比皆是其次是环境保护的需要由于天然砂的无序生产,在生产、储存和运输过程中还造成对空气和环境的污染,国务院和各地人民政府不得不相继出台了禁采或限采天然砂的规定。鉴于实际情况，于2002年月1日起实施的新国标《建筑用砂》（GB/T14684-2001）增加了人工砂为建筑用砂之一，并规定了人工砂的定义、技术要求、检验方法。国内以人工砂等替代天然河砂。今后人工砂将作为建筑用砂的重要来源而挤身于建材市场。 北京兴发水泥厂生产的42.5水泥,主要物理性能指标见表1 表1 水泥主要性能 凝结时间(min) 抗压强度(Mpa) 抗折强(Mpa) 细度(%) 标准稠度用水量(%) 初凝 167 终凝 300 3d 23.5 28d 49.7 3d 4.8 28d 8.9 0.8 27.0 2.2 粉煤灰。石景山电厂二级灰 表2 粉煤灰的主要性能 需水量比(%) 细度(%) 烧失量（%） SO3含量 94 19 2.1 合 格 2.3 人工砂。试验所用人