Ni-P-多壁碳纳米管复合镀层的制备研究毕业论文.doc

毕 业 论 文 自从碳纳米管被发现以来，它所具有的特殊机构和良好的性能，引起了科学家们的广泛关注，碳纳米管复合镀技术也得到迅速发展。但是，由于碳纳米管在水中的浸润性较差，在镀液中不能稳定的分散，导致碳纳米管在复合镀层中分布不均匀，从而影响复合镀层的质量。本实验包括对购买的碳纳米管进行纯化；利用三种表面活性剂(CTAB、曲拉通、十二烷基磺酸钠)对碳纳米管改性；碳纳米管的分散；镀液的配制；对镀件的预处理、化学镀、取样；对样品的观察、分析。 本实验利用化学复合共沉积的方法制备碳纳米管镍磷复合镀层，获得制备均匀分散的镀液，得到理想的镀样效果。 关键词：碳纳米管；表面修饰；表面活性剂；复合镀；共沉积。 毕 业 论 文 外 文 摘 要 Title Preparation of Ni-P-multiwalled carbon nanotube composite coatings Abstract: Since carbon nanotubes were discovered, it has attracted wide attention of scientists because it has the special institutions and good performance. Carbon nanotube composite plating technology has been developing rapidly. However, because of poor wettability of the carbon nanotubes in water and unstable in the presence of dispersed in bath, it resulted in the distribution of carbon nanotubes in the composite coating is uneven. And it affect the quality of the composite coating. The experiment included the purchase of purified carbon nanotubes; Using three surfactants(CTAB, Triton, sodium dodecyl sulfate) on carbon nanotubes modified; A dispersion of carbon nanotubes; Configure preparation;Pretreatment of plating, electroless plating, sampling;Observation of the sample analysis. This experiment by using the method of composite chemical preparation of nickel pHospHorus compound coating, carbon nanotubes for the preparation of uniform dispersion of plating solution, get the ideal effect of plating sample. Keywords: Carbon nanotubes; Surface modification; surfactant; composite plating; co-deposition.  目 录 第一章 绪论 1 1.1 引言 1 1.2 碳纳米管的结构和性质 1 1.2.1 碳纳米管的结构 1 1.2.2 碳纳米管的性质 2 1.3 碳纳米管纯化方法 2 1.3.1 引言 2 1.3.2 碳纳米管纯化方法 3 1.4 纳米复合镀技术研究现状 3 1.4.1 复合镀的定义 3 1.4.2 复合镀的原理 4 1.4.3 复合镀的分类 4 1.5 纳米复合镀层制备影响因素 6 1.5.1 表面活性剂的影响 6 1.5.2 镀液成分影响 7 1.5.3 温度的影响 7 1.5.4 pH的影响 7 1.6 纳米复合镀层的特点与应用 7 1.6.1 纳米复合镀层的特点 7 1.6.2 纳米复合镀层的应用 8 1.7 研究内容 8 第二章 实验仪器与实验方法 8 2.1 实验原理 9 2.2 实验仪器与分析仪器 10 2.2.1 实验仪器 10 2.2.2 分析仪器 11 2.4 实验药品试剂 12 2.5 实验过程 12 2.5.1 碳纳米管的纯化 12 2.5.2