赤泥及其各种改性物对磷和砷的吸附研究.pdfVIP

赤泥及其各种改性物对磷和砷的吸附研究 倪帆 彭先佳 何劲松 王军 栾兆坤 中国科学院生态环境研究中心水质学国家重点实验室，北京 100085 摘要：以铝厂矿渣赤泥为原料，采用焙烧、酸化、盐改性及复合活化的方法进行赤泥改性处理，考察了赤 泥及其改性物对磷和砷的吸附效果。结果表明，活化改性可以明显提高赤泥的吸附能力。焙烧可以提高赤 泥对磷的吸附能力，酸化对除磷效果的影响不如焙烧。盐改性可以明显提高赤泥对砷的吸附能力。将盐改 性和焙烧结合可同时提高赤泥对磷和砷的吸附能力，而酸化与焙烧结合的活化方法不如前者。 关键词：赤泥；活化；吸附 Adsorption of phosphate and arsenic by activated red mud Ni Fan Abstract: Red mud was used as raw material for the removal of phosphate and arsenic. Activation of red mud was carried out by the process of calcination, acidification, salt modification and the combined process. The results showed that the adsorption of phosphate and arsenic was enhanced by activated red mud. Calcination enhanced the adsorption of phosphate. However, acidification was not as effective as calcination. Salt modification enhanced the adsorption of arsenic. Combined salt modification and calcination enhanced the adsorption of both phosphate and arsenic. Besides, combined acidification and calcination was not as effective as the combined process of salt modification and calcinations. Key Words: Red Mud; Absorption; Phosphate; Arsenic 作者简介：倪帆,男,1984.6，中国科学院生态环境研究中心,博士研究生，环境工程专业，主要从事水处理药剂的研发及应用。 联系地址：北京市海淀区双清路 18 号，中国科学院生态环境研究中心环境技术楼 223 室。邮编：100085。电话：010 。 E-Mail: realrice@163.com 铝厂矿渣赤泥在大量堆放引起环境问题的同时，由于其含有较多的铁、铝、钙等成分，对水中磷和砷 具有一定的吸附能力[1, 2] 。然而赤泥吸附能力有限，需要进行活化以提高吸附能力。本实验以铝矿工业赤 泥为原材料，采用焙烧、酸化、盐改性以及相互结合的复合改性方法进行活化，研究了赤泥及其各种改性 物对磷和砷的吸附。 赤泥样品来自山东铝业股份有限公司，自然风干后研磨过 100 目备用，此为原状赤泥。赤泥活化改性 方法主要有焙烧、酸化和盐改性[3] 。其中焙烧活化方法是用原状赤泥，分别在 100℃、300℃、500℃、700℃、 900℃和 1200℃下在马弗炉中焙烧2h 。酸化过程分为冷酸活化和热酸活化。冷酸活化将原状赤泥以20mL/g 的液固比加入0.25mol/L 的盐酸，于反应器搅拌2 h ，水洗三遍滤纸抽滤之后，干燥备用；热酸活化在恒温 水浴锅内进行，反应温度为 80 ℃，搅拌2 h ；酸化焙烧结合的方法为将冷酸活化完毕的赤泥在700℃下在 马弗炉中焙烧 2h 。盐改性方法将原状赤泥、700℃焙烧赤泥、900℃焙烧赤泥加入 1 mol·L - 1 的FeCl2 溶液中， 调