核电站工程阶段大型储罐地脚螺栓的防腐研究.pdfVIP

The 6th China Corrosion Conference Corrosion Resistance Research of Anchor Bolts for Large Storage Tank in Nuclear Power Station Construction Stage Shunchao MIAO, Peipeng QIAO, Gang SHEN Suzhou Nuclear Power Research Institute, Suzhou, China Email ：miaoshunchao@163.com Abstract: By analyzing some anchor bolts failure cases in domestic and foreign nuclear power station, most of them are caused by incorrect material design, improper installation and inappropriate construction. Corro- sion problems that may arise are analyzed and corresponding preventive measures are proposed considering the specific characteristics of anchor bolts in construction stage. Keywords: Construction Stage; Anchor bolts; Corrosion 核电站工程阶段大型储罐地脚螺栓的防腐研究 苗顺超，乔培鹏，申罡 苏州热工研究院有限公司，苏州，中国，215004 Email ：miaoshunchao@163.com 摘 要：通过分析国内外核电站众多地脚螺栓失效案例发现，多数为工程阶段设计选材失误、安装或 防腐施工不当所致。结合电站工程阶段地脚螺栓的现场情况，分析了可能出现的腐蚀问题，并提出了 相应的预防措施。 关键词：工程阶段；地脚螺栓；腐蚀 2006 年 3 月，该电站土建处执行腐蚀状态检查 1 引言 时发现，除盐水分配系统除盐水箱的地脚螺栓出现 地脚螺栓是电站大型设备的重要支撑部分，部分重 较严重的腐蚀，随后及时进行了防腐处理。现场来 要设备的地脚螺栓还有抗震要求。一旦出现腐蚀失效问 看，部分地脚螺栓与地面结合处锈蚀掉接近三分之 题，将会带来严重的安全隐患，甚至影响电站的安全运 一，地脚螺栓腐蚀若进一步加剧，则影响设备的稳 行。地脚螺栓位于储罐的底部，由于结构原因，雨水、 定性和抗震能力。地脚螺栓的腐蚀形貌如图 1 所 酸洗液等腐蚀性介质很容易在地脚螺栓处聚集、浓缩， 示。 形成恶劣的腐蚀环境。严重的腐蚀环境造成地脚螺栓的 腐蚀，给设备的正常使用和电站的安全运行构成了很大 a) b) 的威胁。 工程建设的设计、制造、安装、调试等各阶段产生 的缺陷或隐患通常会是设备腐蚀问题的根源，在此阶 段，需做好充分的防腐管理工作。本文通过分析国内某 在运行核电站的地脚螺栓腐蚀案例，并结合国内某在建 核电站的现场情况，具体提出了相应的预防腐蚀措施和 Figure 1. Corrosion