粘结剂对纯铁磁粉芯性能影响.pdfVIP

21 4 Vol.21 No.4 2011 8 POWDER METALLURGY INDUSTRY Aug. 2011 1 1 1 1 1 2 , , , , , ( 1. , 410083; 2. , 518000) : 采用粉末冶金工艺制备纯铁磁粉芯, 研究了粘结剂含量组成对磁粉芯综合性能的影 结果表明, 粘结剂含量为27% ~ 36%, 无机与有机粘结剂组成为3 2~ 3 1 时, 粘结 剂的包覆效果较好, 样品的力学性能得到较大改善, 抗压强度达到了480 MPa; 粘结剂含量为 28%~ 35% , 无机与有机粘结剂组成为21 时, 磁粉芯磁性能较好, 综合性能较佳 : 粉末冶金工艺; 粘结剂; 力学性能; 磁性能 : TG1322 71 : A : 1006- 6543( 2011) 04- 0042- 07 EFFECT S OF BINDERS ON IRON POWDER CORES COMPREHENSIVE PERFORMANCE 1 1 1 1 1 2 ZHAOLi ,LI Du-xin ,LI Kun ,YANGZhong-cheng , ZHANG i , XU Dong ( 1. The State Key Laboratory for Pow der Metallurgy, Central South U niversity, Changsha 410083, China; 2. Shenzhen TPS Technology Co. , Ltd, 518000, China) Abstract:Pure iron powder cores were fabricated by powder metallurgy technique. Influence of the content and composition of binders on comprehensive performance of the material was researched. Result show s that the mechanical properties of samples are greatly improved and the compressive strength achieves 480 MPa when the total content of binders is 27% ~ 36%, inorganic and organic ratio are 32~ 31, as binder coating get the best effect. Mag- netic properties and comprehensive performance of magnetic cores are the best when total content of binders is 28%~ 35% , inorganic and organic ratio is 21. Key words:powder metallurgy; binders; mechanical properties; magnetic properties , , , [ 1-6] , , , , , , [ 7] ; , , ,