基于ABAQUS 耐火材料细观损伤本构模型开发与实现.pdfVIP

中国科技论文在线 基于 ABAQUS 的耐火材料细观损伤本构模 型的开发与实现# 陈瑶，王志刚，刘昌明** 5 （武汉科技大学机械自动化学院，武汉 430081） 摘要：针对耐火材料复杂的非线性力学行为及其损伤机理，在细观力学基础上提出了基于界 面相模型的耐火材料细观损伤力学模型，利用 ABAQUS 软件的二次开发平台，开发了该本构 关系的子程序.利用该本构模型，对镁碳质耐火材料的受压试验进行了数值模拟.结果表明， 运用该本构模型对耐火材料的非线性损伤力学行为进行模拟与试验结果能够较好的吻合。 10 关键词：耐火材料；本构模型；细观力学；二次开发；ABAQUS 中图分类号：TB35 Secondary Development of Micromechanics Damage Constitutive Model of Refractory based on ABAQUS 15 CHEN Yao, WANG Zhigang, LIU Changming (Machinery and Automation School,Wuhan University of Science and Technology, WuHan 430081) Abstract: According to the complex nonlinear mechanics behavior and the damage mechanisms of refractory materials, damage constitutive model of refractory materials was put forward based on 20 the interphase model by the method of micromechanics. Utilizing the model proposed, a subroutine was developed through the commercial software ABAQUS. Using the subroutine, the damage of the magnesium carbon refractory was simulated under compression. The results of the simulation are in good agreement with the experimental data. Keywords: refractories; constitutive model; micromechanics; secondary development; ABAQUS 25 0 引言 耐火材料作为高温容器件的隔热保温材料，是保障高温设备安全运行的关键.热应力破 坏是耐火材料主要损毁方式之一，数值模拟是研究耐火材料热应力的主要技术手段.本构模 型能否真实反映其力学行为，将直接决定有限元法等数值模拟技术计算的准确性.然而耐火 30 材料的微观非均质性使其物理性能，特别是热机械性能受温度和载荷状况的影响较大，在宏 观上表现为依赖于温度的非线性力学行为. 由于耐火材料力学行为的非线性源可能来自任何 可能的微观变形和损伤机理，因此，建立在连续介质假设基础上的材料本构行为的统一描述 就变得非常困难.到目前为止，仍未找到一种适合于数值模拟的耐火材料力学行为的表征方 法。 35 耐火材料复杂的非线性力学行为，实际上是其微观结构与外载荷相互作