连铸坯凝固组织和缺陷冷酸蚀法宏观检验.pdfVIP

　　　2003 年 　 10 月 炼 　钢 　　Oct . 2003 　　　第 19 卷 第 5 期 Steelmaking Vol . 19 　No . 5 ·26 · 连铸坯凝固组织和缺陷的冷酸蚀法宏观检验 许庆太 　张 　楠 　傅 　强 (鞍山钢铁集团公司) 　　摘 　要 　叙述了冷酸蚀法较硫印和热酸蚀低倍检验方法的优越性 , 冷酸蚀法不但能够显示连铸坯 ( ) 的内部缺陷 , 而且也能够提供连铸坯凝固组织的信息 。它可对连铸坯的内部缺陷原样 尺寸 地显示 。 同时 , 提出了按冷酸蚀法对现行标准进行修改的意见 。 关键词 　冷酸蚀法 　凝固组织 　缺陷 Macroscopic Examination on Sol idif ication Structure and Def ect of Continuously Cast Steel by Col d Acid Etching Xu Qingt ai 　Zhang N an 　Fu Qiang (Anshan Iron Steel Group Corp . ) 　　Abstract 　Advant ages t he cold acid etching p rocess po ssesses in comp arison wit h t he conventional hot acid etching and sulp hur p rint are described . Practical operation result s indi cate t hat t his p rocess can not only display t he inner defect s in original size in t he continuously cast steel , but also p rovide information about t he solidification st ruct ure of t he steel . At t he same time t he p ropo sals necessary for up dating t he current st andar ds are p ut forwar d in t he p resent p aper . Key words 　cold acid etching 　solidification st ruct ure 　defect 2002 年 3 月末 , 两年时间为鞍钢第一炼钢厂检验 1 　前 　言 280 mm ×280 mm 方坯和 280 mm ×380 mm 矩 ( ) ( 对连铸坯来说 , 尽管其凝固组织与传统模铸 形坯共 1 635 块 , 230 ～300 mm × 1 650 ～ 相比无本质差别 , 也是由激冷层 、柱状晶和中心 2 000) ( )