*铣削GLGQXX新型高强度铝合金 表面粗糙度的研究 摘要：GLGQXX高强度铝合金材料的加工质量直接关系到其应用与推广,通过采用正交试验研究了铣削参数对GLGQXX新型高强度铝合金工件表面粗糙度的影响，得出了各参数对表面粗糙度影响的主次顺序及影响规律，最后运用MATLAB计算得出了表面粗糙度经验公式，可为GLGQXX新型高强度铝合金的铣削参数选择提供参考。 关键词：表面粗糙度；铣削参数；正交试验 ；经验公式 中图分类号：TG54 文献标识码：A *The research of surface roughness for milling GLGQXX high strength aluminum alloy The processing quality of high strength aluminum alloy material GLGQXX is directly related to its application and promotion, using orthogonal test to study the relationship between the milling parameters and surface roughness of LGQXX high strength aluminum alloy.then analyzes the test results,the effect of various parameters on surface roughness is obtained.and finally ,the roughness empirical formula calculation.was established by using MATLAB. Provide reference to select milling parameters for GLGQXX model of high strength aluminum alloy. Keywords: surface roughness, milling parameter, orthogonal test，emprical formula (0 引言 表面粗糙度描述的是加工表面上微小峰谷不平度和较小间距微观几何形状的尺寸特性，反映的是切削参数与系统变量的综合影响，是衡量切削加工表面质量的重要指标[1]。 GLGQXX高强度铝合金是一种新型高塑性高强度铝合金材料，具有非常广阔的市场前景。一方面，其强度相当于正火和退火状态低中碳钢，具有极强的变形能力和塑性。另一方面，GLAQXX高强度铝合金中添加了稀土元素，因此它的切削加工具有特殊性。铣削是铝合金材料常见的加工方式，研究铣削参数对表面加工质量的影响，得出了铣削参数对表面质量的影响规律。 1 实验方案设计 本实验采用高速钢铣刀铣削试件表面，运用正交分析法设计试验。 主要实验条件如下： 刀具：高速钢立铣刀。规格：，前角：12o，后角：20o，螺旋角：35o，齿数：4。机床：铣床VM600，相关参数为：行程:600×410×510mm（纵向横/向/垂向）；工作台面积：800×400mm；工作台最大承重：700kg；定位精度0.005mm。工件：GLGQXX新型铝合金长方体试件，长160×宽100×高30。测量仪器：HSR金刚石触针三维轮廓测量仪。 在实验中，以零件表面粗糙度为实验指标，以切削速度、切削深度、每齿进给量为影响因素。根据正交试验表设计正交试验。因素水平表如表1所示。 表1 因素水平表 水平 因素 （r/min） （mm/z） （mm） （mm） 1 2000 0.01 4 0.5 2 2500 0.02 5 1 3 3000 0.03 6 1.5 4 3500 0.04 7 2 2 实验结果及分析 2.1 正交实验结果 表2 正交试验结果 序 号 因素 实验结果 （r/min） （mm/z） （mm） （mm） （） 1 2000 0.01 4 0.5 0.298 0.33 2 2000 0.02 5 1 0.495 0.602 3 2000 0.03 6 1.5 0.536 0.686 4 2000 0.04 7 2 1.681 1.609 5 2500 0.01 5 1.5 0.401 0.657 6 2500 0.02 4 2 0.910 0.644 7 2500 0.03 7 0.5 0.72 0.673 8 2500 0.04 6 1 0.499 0.817 9 3000 0.01 6 2 0.416 0.501 10 3000 0.02 7 1.5 0.533 0.444 11 3000