高温螺栓断裂分析.docVIP

中国科技论文在线 25Cr2MoV钢高温螺栓断裂分析 刘建华 （中国矿业大学材料科学与工程学院，江苏 徐州 221116） 摘要：通过力学性能试验、金相分析及 SEM断口分析对火电厂机组气缸 25Cr2MoV钢高温紧 固螺栓发生断裂进行了研究。结果表明：该螺栓长期在高温条件下服役，其晶界会有黑色网 状碳化物析出、晶界粗化，同时组织老化，承受载荷能力下降。在停开机提速过快时，螺栓 不能承受施加的偏心冲击载荷，导致其发生脆性失效。 关键词：25Cr2MoV；脆性断裂；断口分析；晶界弱化 中图分类号：TG142.1 The Fracture Analysis of High-temperature Blots Made of 25Cr2MoV Steel LIU Jianhua (School of Material Science and Engineering,China University of Mining and Technology, JiangSu XuZhou 221116) Abstract: The fracture of high-temperature fastening blots made of 25Cr2MoV steel used on thermal power unit cylinder has been studied.Analyses on fracture with mechanical properties, metallographic examination and SEM have been carried out. The results showed that the black mesh grain boundary carbide precipitation with 25Cr2MoV steel under long-term elevated temperature service, and the grain boundary coarsening.These factors contribute to grain boundary and grain boundary weakening performance, organization of aging itself ,load bearing capacity of the matrix decreased. Stop the excessive speed at the start, the bolts can not withstand the impact loads imposed by the eccentric, leading to brittle failure. Keywords:25Cr2MoV; brittle fracture; fractography analysis; grain boundary weakening 0引言 火力发电厂锅炉、汽轮机的气缸结合面和蒸汽管道等部件广泛采用 25Cr2MoV钢高温 螺栓进行紧固连接 [1]。实践表明，该螺栓长期在高温下运行，常出现脆化现象，其硬度明显 升高，室温冲击韧性下降，发生断裂，直接影响火电厂的生产安全 [2,3]。为此原水电部曾颁 布标准规定， 25Cr2MoV螺栓硬度超过 HB240～270 ，室温冲击韧性小于 588kJ / m2，就 不能再使用，可以进行重新热处理 (称恢复热处理 )使螺栓韧性得到恢复 [4]。该螺栓要具有良 好的耐热性和抗松弛能力，低的热脆性，且在常温下有高的强度和冲击室温韧性 [5,6]。 1试验材料和方法 1.1试验材料 本文试验材料由某发电厂提供的已发生断裂的 25Cr2MoV钢机组汽缸紧固螺栓，其规 格为 M100×4×1085，工作温度 540℃左右，压力 13MPa。经材质分析，该螺栓材料的化学 成分和标准技术要求如表 1所示。 1.2试验方法 从断裂的高温螺栓断裂面靠近杆体侧沿纵向取样，拉伸试验按照国家标准 GB228-2002 执行，在 CSS-44300电子拉力试验机上进行，采用 Φ10×50mm标准拉力试样，试样数量为 作者简介：刘建华，（ 1987-），男，硕士研究生，金属材料的失效分析 . E-mail: liujh2005.12@163.com - 1 -  中国科技论文在线 3个。冲击性能测试按照《金属材料夏比摆锤冲击试验方法》 (GB/ T229 —2007) (以下简称 《冲击试验》 )的规定 [7]，在 JNB-300B试验机上进行，同拉伸试验取相同部位的的材料， 采用 10×10×50mm标准 U型和 V