The study of wetting ability of the fine zirconia ceramic membrane before and after laser ablation Sun Defeng , Zhang Cunlin, Chen Wen, Yang Xiaoyi Capital Normal University Physics Department, 100037 Abstract: The fine nanostructure yttria stabilized tetragonal phase zirconia membrane is prepared by sol-gel method and the wetting ability of the ceramic thin film before and after laser ablation is discussed. The results show that the wetting ability depends on the content ratio of O to Zr on the membrane surface. The smaller the ratio is, the better the wetting ability is. The oxygen deficiency occurs after laser treatment which makes the value O/Zr small. At this time, water can spread on the membrane surface. So, the membrane exhibits hydrophilicity after laser ablation. After a month aging, the oxygen in the air is absorbed onto membrane surface which makes the value O/Zr large and the water can not spread on the membrane surface. Keywords: zirconia ceramic membrane, wetting ability, laser ablation, oxygen deficiency ZrO2 ZrO2 1 2 1064nm YAG 1. · · 1mol/l 0.5mol/l