包芯线喂线速度的理论探讨 1 1 2 1 2 2 1 颜根发 ，黄志勇 ，谢志强 ，徐广治 ,金进文 ,杨利康 ,夏晶晶 (1. 马鞍山中冶高新技术公司，安徽 马鞍山 243002 ；2. 杭钢转炉炼钢厂) 摘要 运用相似理论，把数学解析方法与试验方法结合在一起,通过对包芯线喂入钢液过程传热特征的分析，推导出包芯线 熔化时间 τ 。再根据为了提高包芯线中合金的收得率，应将包芯线喂入钢液“尽可能的深处”时才完全熔化，这个钢液“尽可能 的深处”，一般离钢包底 300 mm 左右，进一步从理论上推导出包芯线的喂线速度方程式。 关键词 包芯线 喂线速度 The Oretical Discussion on Injection Speed of Cored Wire 1 2 2 1 Yan Genfa , Huang Zhiyong , Xie Zhiqiang , Xu Guangzhi 1 1 2 Jin Jinwen , Yang Likang , Xia Jingjing (1. Maanshan MCC High-tech Co., Ltd., Ma’anshan, Anhui, 243002; 2. Hangzhou Steel Converter Steel Works) Abstract Using similarity theory, in combination of mathematical analysis methods and test methods, through analysis on heat transfer characteristics of the process of injecting cored wire into liquid steel, the melting time t of cored wire is deduced. Additionally, in order to enhance the alloy yield in cored wire, the cored wire shall be injected into the liquid steel “as deep as possible” so as to be molten completely, and such liquid steel “as deep as possible” is generally about 300mm away from the ladle bottom, thus the equation of injection speed of cored wire is further deduced theoretically. Key words Cored wire Injection speed 为了提高包芯线中合金的收得率，应将包芯线喂入钢液“尽可能的深处”时才完全熔化。这个“尽可能的 深处”，一般离钢包底 300 mm 左右。喂包芯线线技术的关键之一就是在了解包芯线熔化时间和将包芯线喂 [1] 入钢液“尽可能的深处” 的基础上,确定相应的理论喂线速度。过去有些文献报导 ,采用数学解析方法，建立 非稳态传热微分方程，但求解这个方程很不方便。为此，笔者运用相似理论，把数学解析方法与试验方法 结