焊接工艺指导书Ⅱ.docVIP

焊接工艺指导书Ⅱ WPS II 编制： Organization.: 审核: To examine : 无锡金波隔振科技有限公司 Wuxi Jin Bo Isolation Technology Company Limite 二〇一一年三月 2011，March 1 设备及人员 equipment and personnel 1.1 设备：氩弧焊机。 Equipment: argon arc welding machine. 1.2 焊接人员须经焊工培训合格后方可上岗操作。 Welding personnel shall be subject to approval by the welder training eligible and rear but mount guard operation. 2 焊前准备Preparation before welding 2.1 焊前先将各零件按设计图的要求进行尺寸和外观检查，检查合格后方可进行焊前清洗工作。Welding before each part according to the design requirements of size and appearance inspection, inspection before cleaning before welding work. 2.2 将所用焊丝剪成0.5米左右长的焊丝，校直并用丙酮清洗干净；允许用母材剪成2mm×2mm代替焊丝，用丙酮擦洗后焊接。That will be used by wire cut into about 0.5 meters long wire, straightening with acetone and clean; allow the use of parent material cut into 2mm x 2mm instead of wire, with acetone scrubbed after welding. 3 焊接型式：Welding type: manual argon arc welding 焊接特性：直流正极性Welding characteristics: positive DC 钨极材料：wce20 Tungsten material: wce20 保护气体：氩气 99.99%Protective gas：Argon 99.99% 4 记录Record 做好记录，按电流电压记录。Good welding records, according to of welding current and voltage of QR / JB7.5.2-01 records. 接头型式Joint type t×z 材 质Texture of material 填充金属 （焊丝牌号）Filler metal wire grade 焊丝 直径Wire diameter 电流Electric currentA 电弧电压 Arc voltageV 钨极 直径Tungsten electrode diameter 氩气流量Argon flow （l/min A B 0Cr18Ni10Ti 0Cr17Ni12Mo2 H1Cr24Ni13Mo2 00Cr17Ni14Mo2 H0Cr26Ni21 0.3×3 0Cr18Ni9 H1Cr24Ni13 φ2.0 90-110 0Cr18Ni10Ti 0Cr17Ni12Mo2 H1Cr24Ni13Mo2 00Cr17Ni14Mo2 H0Cr26Ni21 0.3? 0Cr18Ni9 H1Cr24Ni13 100-120 0Cr18Ni10Ti 0Cr17Ni12Mo2 H1Cr24Ni13Mo2 00Cr17Ni14Mo2 H0Cr26Ni21 0.5? 0Cr18Ni9 H1Cr24Ni13 80-100 12-14 0Cr18Ni10Ti 0Cr17Ni12Mo2 H1Cr24Ni13Mo2 00Cr17Ni14Mo2 H0Cr26Ni21 接头型式Joint type t×z 材 质Texture of material 填充金属 （焊丝牌号）Filler metal wire grade 焊丝 直径Wire diameter 电流Electric currentA 电弧电压Arc voltage V 钨极 直径Tungsten electrode diameter 氩气流量Argon flow （l/min A B 0Cr18Ni10Ti 0Cr17Ni12Mo2 H1Cr24Ni13Mo2 00Cr17Ni14Mo2 H0Cr26Ni21 0.5×3 0Cr18Ni9 H1Cr24Ni13