毕业设计（论文）-骨料对高铝质低水泥浇注料性能的影响研究.docVIP

摘 要 关键词： Abstract In order to improve the physical properties of high alumina castables, this thesis aggregate castable high alumina preparation conditions for the study of the system. Reasonable experiment to develop appropriate experimental preparation of the sample, and samples for heat treatment, testing the mechanical properties of the sample through the analysis of experimental results discussed to identify the aggregate and high alumina low cement castable, recipe the relationship between the composition and technical parameters, analysis of the mechanism, focuses on the impact of aggregate on high alumina low cement castable, the relationship between the system and its physical properties, and thus high alumina low cement castable optimization components, to achieve the best economic use of effects. The results show that: Aggregate type on the strength and density of the castable mainly by the mechanics and high-temperature sintering performance of the decision, and the aggregate species relative to the particle shape and surface characteristics of fluidity is smaller. Spherical particles will help to improve the fluidity of the castable, but other physical properties of the castable. Aggregate size composition had a greater influence on the physical properties of castable aggregate size 8 5mm: a 3mm 5: 3 a 1mm = 10:20:20 castable better. Of aggregate particles while mullite and grade bauxite combined with the overall best. Cement castables drying intensity; Add microsilica to improve mobility and sintering of the casting material, and thus make castable temperature strength with improved performance; molding water content more than castable increase , but will castable other physical properties have a greater adverse effects. Keywords:High alumina low cement castable; aggregate; castable composition; physical properties 目 录 第一章 文献综述 1 1.1耐火浇注料的定义及其发展 1 1.1.1耐火浇注料的定义及特点 1 1.1.2耐火浇注料的发展概述 2 1.2高铝水泥的性