四川理工学院毕业论文 过硼酸钙的研制 学 生：王 晓 龙 学 号：09031010215 专 业：化学工程与工艺 班 级：2009级2班 指导老师：汤秀华 四川理工学院材料与化学工程学院 二〇一三年六月 摘要 本文研究了以硼砂和氢氧化钙为原料在不同质量配比和反应温度下，合成中间产物偏硼酸钙。在稳定剂作用下，以偏硼酸钙和30%的双氧水反应制备过硼酸钙，主要考察了反应温度、反应时间、液固比等因素对合成最终产物过硼酸钙的收率、活性氧含量的影响。研究结果表明：在硼砂/氢氧化钙=100：2235℃下，更有利于合成偏硼酸钙；合成过硼酸钙的优化工艺条件为：反应温度为70℃，反应时间为40 min，反应液固比（mL/g）4：1 关键词：偏硼酸钙；过硼酸钙；活性氧；得率 Abstract In this paper, the borax and calcium hydroxide as raw materials in different quality ratios and reaction temperature,synthesis of intermediate product calcium metaborate was studied. Under the effect of stabilizers, calcium perborate was synthetised with calcium metaborate and hydrogen peroxide(30%). The effects of reaction temperature, reaction time, liquid-to-solid ratio on the synthesis of the final product of calcium perborate yield and active oxygen content was inspected mainly. The experimental results showed that: the borax/calcium hydroxide=100:22 and 35℃ was more conducived to the synthesis of calcium metaboratel;synthesis of calcium perborate to optimize process conditions as follows: reaction temperature was 70℃, the reaction time for 40 min,the liquid-to-solid ratio(mL/g) was 4:1. Key words ：Calcium metaborate；Calcium perborate；Active oxygen；Yield  目 录 第一章 绪 论 1 1.1 引言 1 1.1.1 研究背景 1 1.1.2 研究意义 1 1.1.3 研究目的 2 1.2 过硼酸钙的简介 2 1.2.1 过硼酸钙的性质 2 1.2.2 过硼酸钙的应用 3 1.2.3 过硼酸钙的制备方法 4 第二章 实验部分 5 2.1 实验试剂及仪器 5 2.2 实验分析方法 6 2.2.1 氧化硼（B2O3）含量的测定 6 2.2.2 氧化钙（CaO）含量的测定 7 2.2.3 过硼酸钙中活性氧含量的测定 9 2.3 合成工艺流程图 10 2.4 实验步骤与方法 10 2.4.1 实验步骤 10 2.4.2 实验思路 11 2.5 实验原理 11 2.6 产品得率的表示与计算 12 第三章 实验结果与分析 13 3.1 单因素实验 13 3.1.1 研究实验反应条件对中间产品的影响 13 3.1.2 研究不同工艺条件对最终产品的影响 17 3.2 正交实验分析 21 第四章 结论 23 参考文献 24 致 谢 25 第一章 绪 论 1.1 引言 1.1.1 研究(1)虽然我国是世界上硼资源较丰富的国家之一, 但是目前能加工利用的硼只占总储量的10%，由于国内没有较成熟工艺的加工的原因,所以就一直没能形成大规模的工业开发和利用；(2)(3)贫矿较多且品位低。正是因为硼矿石资源较少,国内很多硼化物生产企业不得不使用品位很低（10%）[7]。 我国是世界上最早发现和最先使用天然硼砂的国家，有较丰富的硼自然资源，且有一定的初级经验水平。但是，在中国历史上我国并没有建立形成自己的硼工业，并没有生产出一系列硼化物。而在最近两年，我国的硼化物生产企业逐渐萌芽，科学地调整硼产品结构