（5）绿色建筑与生态环境材料 定形相变材料的导热性能研究* 王少胤，陆海旭，陈龙，杨睿 （清华大学化工系，北京，100084） 摘 要：在定形相变材料中添加导热增强填料，可以有效提高其导热性能。本文以膨胀石墨和碳纳米管作 为导热增强填料，采用不同的填料分散和加工工艺，改变填料在定形相变材料中的分布状况，以期达到调 控材料导热性能的目的。研究结果表明，由于两种填料不同的形貌特征，膨胀石墨采用简单超声处理即可 达到较好效果，而碳纳米管则必须要通过强剪切才能实现较好分散。膨胀石墨和碳纳米管之间可能存在协 同作用。当膨胀石墨含量达到7wt%时，定形相变材料的导热系数可提高约4 倍。 关键词：材料学；相变材料；导热性能；膨胀石墨；碳纳米管 Thermal conductivity of shape-stabilized phase change material WANG Shaoyin, LU Haixu, CHEN Long, YANG Rui (1. Department of Chemical Engineering, Tsinghua University, Beijing, 100084) Abstract：Introducing fillers with good thermal conductivity into shape-stabilized phase change materials (SSPCM) is an effective way to improve the thermal conduction performance of SSPCM. In this paper, expanded graphite and carbon nanotube were selected. Ultrasonic treatment and shear dispersion of these two fillers were applied to help their dispersion in SSPCM matrix, and thus change the thermal conductivity. The results showed that for expanded graphite, ultrasonic treatment was enough to achieve good dispersion, and shear treatment made the worm-like structure broken. For carbon nanotube, relatively good dispersion could be achieved only by strong shear. Synergistic effect may exist between expanded graphite and carbon nanotube in enhancing the thermal conductivity. The thermal conductivity of SSPCM increased by 4 times with 7wt% expanded graphite. Key words ：materialogy ; phase change material; thermal conduction; expanded graphite; carbon nanotube 0 引言 在自然界化石能源日趋枯竭的今天，清洁和可再生的自然能源如太阳能的综合利用受到 了人们越来越多的关注。无论是太阳能发电还是太阳能供热，一个共同的突出问题就是能量 供应的不连续和不稳定性。因此，高效的能量储存系统和储能材料对于太阳能利用非常关键。 相变材料（主要是固-液相变材料）在相变过程中可以吸收大量的热，同时温度保持基本不 变，因此是一种非常有潜力的太阳能储热材料。为了方便使用，相变材料可以与高分子基体 共混，形成定形相变材料，以避免吸热之后变成液态泄漏损失或腐蚀管道等。但是，由于相 变材料，尤其是有机相变材料的导热性能较差，储放热效率低，影响了使用效果，因此需要 对相变