热分析法在无取向硅钢相变研究中应用.pdfVIP

热分析法在无取向硅钢相变研究中的应用 李俊虎1 （太原钢铁公司技术中心，太原 030003 ） 摘 要 本文应用热分析方法测定无取向硅钢相变温度、相变潜热变化及化学成分对其相变的影响。结果表明：无 取向硅钢中 Si、Mn、Al 等主要元素发生微小变化，DSC 特征峰的形态与位置会发生显著的改变；在无取向硅钢相 变过程中，潜热的变化量与相变前后的结构状态有直接关系。 关键词 热分析 无取向硅钢 相变 Application of DSC in Transformation of Non-oriented Silicon Steel Li Junhu (Taiyuan Iron and Steel Co., Ltd., Taiyuan, 030003) Abstract Thermal analysis technology has been used to meature transformation temperature and latent heat during transformation,and more, the influence of chemical composition on transformation of non-oriented silicon steel was investigated. The results show that the shape and position of characteristic peak by DSC analysis will Change greatly, with changes of main element of Si,Mn,Al content in non-oriented silicon steel.Variations of latent heat during transformation depend on the state before and after the phase transition. Key words thermal analysis, non-oriented silicon steel, transformation 热分析是用于描述物质的性质与温度的关系的一类技术，由于它具有灵敏、快速、准确等优点，被广泛 应用于材料科学与工程、物理和化学学科等研究领域。 无取向硅钢的相变过程影响其组织与性能，因此掌握无取向硅钢的相变过程，对控制其微结构，提高无 取向硅钢的性能有着重要的理论与现实意义。无取向硅钢相变主要是 F-A 之间相变，无取向硅钢的生产工 艺也紧紧围绕相变进行。DSC 法是研究相变的有力工具，本文用该方法精确测定无取向硅钢相变温度，并 对无取向硅钢特征 DSC 曲线进行解析，确定无取向硅钢中主要化学组分对相变温度的影响，分析了无取向 硅钢相变温度与相变潜热以及热焓变化曲线。所得结果为丰富了无取向硅钢的相变研究，并为制定该类钢种 的热加工工艺提供一定的参考依据。 1 仪器与实验条件 实验用仪器为德国耐驰公司生产的 STA449 C 型同步热分析。实验条件：控温速率为 10℃/min ，气氛： 李俊虎，男，本科，工程师，从事金属材料开发，lijh1@ 第八届（2011 ）中国钢铁年会论文集 氩气保护，参比与样品容器为α-Al O 坩埚。 2 3 2 结果与讨论 2.1 无取向硅钢相变过程在热分析特性曲线上的特征解析 DSC 特性曲线基本分两双与四峰两大类（见图 1、图2 ）。 图 1 无取向硅钢典型双峰特征 图2 无取向硅钢典型四峰特征 形成原因分析：特定成分的无取向硅钢的 DSC 特征曲线在穿越相界处