改性剂对木塑复合材料性能的影响研究 Image Posted by -- on 11/07/06 04:27 PM, updated on 07/29/08 09:40 AM 许民　李坚 摘　要：采用木纤维分别与PE、PS、ABS、SAN 等制成木塑复合材料，研究了不同改性剂对木塑复合材料性能的影响，结果表明：改性剂的加入能使木纤维与塑料很好地交接，改性剂不同对复合材料的性能产生不同的影响，木塑复合材料既保持了木质材料原来的优良品质，又具有塑料的一些性能，其防水性、尺寸稳定性、力学强度等均有较大改善。关键词：木纤维，热塑性高分子聚合物，木塑复合材料，改性剂，力学性能 Research of Modifiers’ Effect on the Properties of Wood-polymer CompositesXu Min? Li Jian Abstract: Wood-polymer composites (WPC) were prepared from wood fiber, PE, PS, ABS, SAN. The effects of different modifiers on the mechanical of the composites were studied. The results showed modifiers can make the bond strength between wood fiber and polymer better and different modifiers produce different effects on Wood-polymer composites properties . Composites have the advantages of both wood fiber and polymer. In addition, it improves composites’ waterproof, dimensional stability and dynamic strength.Keywords: wood fiber, thermoplastic polyester, wood-polymer composites, modifier , the mechanical properties　　木塑复合材料（Wood-polymer composites）是由木材和塑料通过一定的工艺复和而成的材料，简称WPC，它具有硬度大、强度高、耐磨、美观、尺寸稳定性好等优点。WPC 自20 世纪60 年代问世以来，一直备受各国学者和企业界的重视，特别是近几年来，由于高分子材料工业的迅猛发展，废旧塑料的回收利用已成为不可忽视的问题。另外，森林资源日趋匮乏，林产品的成本、尺寸稳定性等问题，也迫使人们不断加强对木塑复合材料的研究。有关专家指出，21 世纪木材产品的优先发展领域之一，就是提高附加值的适应于不同场合的木塑复合材料。如何提高木塑复合材料的产品质量、降低成本、改善操作条件，对废旧塑料回收利用和速生劣质木材应用的开发有重要意义。1 试验材料与方法1.1 试验仪器　　高速涡流多用磨粉机，50t 试验预压机，100t 试验热压机，自制旋转拌胶机，AG-10TA 岛津万能试验机，LJ500 型抗张力试验机。1.2 试验材料　　木纤维、塑料（PE、PS、ABS、SAN）、过氧化二异丙苯、异氰酸酯胶、丙酮。1.3 试验方法1.3.1 木纤维的处理　　用搅拌机将木纤维打碎，并干燥至含水率为15%，用薄膜塑料袋密封，备用。1.3.2 塑料的处理　　用高速涡流多用磨粉机将塑料粉碎，由于粉碎后的塑料体积大小不一，很难和木纤维混合均匀，故分别用20 目、34 目筛子筛出，使其体积大小均一，能够得到均匀的塑料、木纤维混合物。1.3.3 板坯的制备　　先将木纤维投入到旋转式拌胶机中，喷入过氧化二异丙苯或丙酮和异氰酸酯胶配比的溶液，旋转数圈后再加入20 目或34 目塑料，使其充分混合均匀，把均匀的混合物利用手工铺装成320mm×340mm 的疏松板坯，然后在室温状态下进行预压，预压压力为1Mpa，时间30s。然后取出放入热压机中进行热压，热压压力（高压12MPa，低压4MPa），热压时间（高压4min，低压6min），热压温度控制在175℃。为防止塑料熔融时发生“粘板”现象，用耐200的高温聚酯膜（0.1mm厚）贴于板坯表面，复合板最终厚度控制在11mm。1.3.4 检测方法　　将热压制成的复合板锯制成320mm×50mm 的长板五块，并编号。取第2、4 块并锯制成50mm×50mm 的试件八块，编号后，前三块测内