变质系列锰钢耐磨性的研究.docVIP

变质系列锰钢耐磨性的研究朱瑞富　吕宇鹏　李士同　朝志强　王世清(山东工业大学)王晓燕(青岛大学) 摘　要　研究了变质系列锰钢的耐磨性与磨面硬度、磨面组织、主要磨损机制及磨损冲击功之间的关系。结果表明，不同成分变质锰钢的耐磨性与磨损冲击功之间呈抛物线关系，耐磨性峰值的位置随锰含量的降低而向较低磨损冲击功方向移动；与耐磨性峰值对应存在着一个“最佳磨面硬度范围”和“适配冲击功范围”，在此范围内材料的耐磨性最高，主要磨损机制为显微切削+浅小凿坑+轻微剥落；钢中形成适量的形变诱发马氏体有利于耐磨性的提高。关键词　锰钢　变质处理　耐磨性 STUDY ON WEAR RESISTANCE OF INOCULATED MANGANESE STEELSZHU Ruifu　LU　¨ Yupeng　LI Shitong　CHAO Zhiqiang　WANG Shiqing(Shandong University of Technology)WANG Xiaoyan(Qingdao University) ABSTRACT　The relation between wear resistance and worn surface hardness, worn surface structure,main wear mechanism as well as wear impact energy has been studied systematic-ally in this paper. The results show that the relation between the wear resistance and wear impact energy of inoculated manganese is of parabolic character.The position of the peak value of wear resistance shifts to lower wear impact energy with reduction in manganese content.“The range of optimum worn surface hardness”and“the range of proper impact energy”are corresponded to the peak value of wear resistance. In these ranges, the wear resistance of the steels is the highest,and the main wear mechanism is of microcutting,shellow impact pitting and slight stripping.A suitable amount of deformation induced martensite is favorable to the improvement of wear resistance.KEY　WORDS　manganese steel,inoculation treatment, wear resistance　　材料的耐磨性具有系统特性，而不是材料固有的属性［1，2］。材料因素、磨料因素、材料和磨料的接触方式、接触应力的大小以及环境因素等都将影响材料的磨损行为［3，4］。本文将研究不同成分的变质锰钢在不同冲击功下的耐磨性与磨面硬度、磨面组织、主要磨损机制及磨损冲击功之间的对应关系，为该类材料的研究、生产及使用提供理论和试验依据。1　试验方法　　试验材料采用150 kg中频碱性感应电炉熔炼，精密铸造，用SR变质剂进行变质处理。试样的化学成分见表1。试样经880 ℃×2 h+550 ℃×3 h+1050　℃×2 h的弥散处理，获得奥氏体基体中弥散分布有颗粒状碳化物的显微组织。 表 1　试样的化学成分　　%Table 1　Chemical composition of samples　　% 钢号 C Mn Si P S SR变质剂 Mn12-1.2 C(SR) 1.23 12.31 1.18 0.070 0.049 适量 Mn10-0.8 C(SR) 0.80 9.98 0.96 0.066 0.044 适量 Mn8-0.8 C(SR) 0.82 8.09 0.88 0.063 0.041 适量 Mn6-0.8 C(SR) 0.81 6.21 1.03 0.059 0.038 适量 　　耐磨性试验在MLD—10型动载磨料磨损试验机上进行。试样尺寸为10 mm×10 mm×30 mm；所选磨损冲击功分别为0.5、1、1.