TC4钛合金的TIG焊接工艺及缺陷分析.pdf

焊接 　2005 ( 12) 　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　 ·55 · TC4 钛合金的 TIG 焊接工艺及缺陷分析 ( ) 长春工业大学材料科学与工程学院 130012 　　赵 　宇 　吉日嘎兰图　陈　莉 摘要 　研究了4 mm 厚 TC4 钛合金板的 TIG 焊工艺及接头力学性能和其焊缝金相组织 ,并对相应的焊接缺陷 做了分析 ,总结出焊接电流为 100～120 A 时 ,焊缝质量最佳 ,接头力学性能也良好 。 关键词 : 　TC4 合金 　TIG 焊 　缺陷　显微组织 TIG WELD ING TECHNOLO GY AND D EFICIENCY ANALYSIS OF TC4 TITANIUM ALLOY Changchun University of Technology 　　Zhao Yu , Jirigalantu , Chen Li Abstract 　The TIGwelding technology of 4 mm thick TC4 titanium alloy plate and the mechanical properties and metallogra phy structure of the joint were studied as well as the welding deficiency was analyzed in this paper . It was concluded that when the welding current was in the range of 100～120 A , the best welding quality and mechanical properties of the joints were obtained. Key words : 　TC4 alloy , 　TIG welding , 　deficiency , 　microstructure 其应用带来一定困难[3～5 ] 。本论文的目的是通过一系 0 　前 　　言 列的焊接试验来研究分析 TC4 钛合金 TIG 焊工艺及焊 TC4 钛合金由于其比强度高 ,具有 良好的室温 、高 接时出现的各种焊接缺陷。 温及低温力学性能 ,且在多种介质中有优异的耐蚀性 , 因而广泛应用于宇航 、舰船 、兵器以及化工等领域[ 1 、2 ] 。 1 　试验过程 从简化结构 、减轻重量等角度出发 ,钛合金的焊接早已 1. 1 　试验材料 成了不可代替的加工手段 。但由于钛及钛合金在高温 本试验使用的母材为 4 mm 厚 TC4 板材 ,焊接材料 下对氧 、氮 、氢和碳等具有极大的亲和力 ,这给焊接带 选用了 2 . 5 mm 的 TC4 标准焊丝 ERTi - 6Al - 4V ,具体 来一定困难 , 同时 , TIG 焊存在熔深浅 、焊接效率低 ,给 化学成分如表 1 所示 。 ( ) 表 1 　TC4 合金母材及焊丝化学成分 % 材料