混凝土抗碳化性能的研究.pdfVIP

商品混凝土 2010年第6期 Beton Chinese Edition ——Ready-mixed Concrete 研究探索 混凝土抗碳化性能的研究 徐海涛，覃爽 （上海隧道工程股份有限公司混凝土分公司，上海 200023） [ 摘要 ] 混凝土的抗碳化能力是衡量地下结构混凝土耐久性的重要指标。本文研究各因素对混凝土抗碳化性能的影响。结果表明 ： 显著性排列为 ：水胶比 掺合料总量 矿粉与粉煤灰的比 ；水胶比增大，混凝土抗碳化能力变弱 ；掺合料总量、矿粉与粉煤灰比 例增加，混凝土抗碳化能力先升后降，40% 掺合料、 Sl∶F=4∶1 时最佳，56d 快速碳化深度小于 10mm，耐久年限可达 100 年以上。 [ 关键词 ] 混凝土碳化 ；耐久性 ； 掺合料 Research on the resistance carbonation ability of concrete Xu Haitao,Qin Shuang (Shanghai Tunnel Engineer Company. Concrete Branch, Shanghai 200023) Abstract: Concrete anti-carbonization ability was a key durability index of the concrete structure. The effects of various factors on concrete resistance carbonization ability were studied in this paper. The signifi cance arrangement: Water-binder ratio total quantity of admixture ratio of slag to ash. Concrete anti-carbonization ability raised, when Water-binder ratio increases. However, it raised fi rst and fell later, when total quantity of admixture or the ratio of slag to ash increases. With total quantity of admixture 40% and he ratio of slag to ash 4:1, 56 days of rapid carbonization depth less than 10mm, the concrete endurance life was more than 100 years. key words: concrete carbonization; durability; admixture 1 概述 矿渣粉 ：S95，上海宝田矿粉厂。 粉煤灰 ：FII，上海环能粉煤灰厂。 随着上海轨道交通和隧道工程的迅速发展，涌现出了一大 外加剂 ：LEX-9p，上海建研外加剂厂。 批的地下工程。地下结构所处环境相对封闭，空气对流较差，