施工技术刊载-水泥基灌浆料产品的发展.docVIP

水泥基灌浆料的发展 朱卫华 （上海宝冶工程技术有限公司 上海 200941） 【摘要】：水泥基灌浆料加水拌合后具有流动性好、微膨胀、早期和后期强度高、不泌水等性能。论述了灌浆料相关标准的发展过程，以及材料性能的发展情况。经过多年的快速发展，高强无收缩灌浆料除了在设备基础二次灌浆上应用外，已经在混凝土结构改造和加固工程及铁路桥梁工程中广泛应用。 【关键词】：建筑材料；灌浆料；标准；应用 【中图分类号】TU521.26 【文献标识码】A 【文章编号】1002-8498（2009）06-0076-02 Development of Cement-based Grouting Material Zhu Weihua (Shanghai Baoye Engineering Technology Co.,Ltd. ,Shanghai 200941,China) Abstract: Cement-based grouting material mixed with water has some characteristics of good fluidity, micro-expansibility, high early and later strength and no bleeding. The author shows developing procedure of correlation standards on grouting material, and developing condition of performances of grouting material. With quickly developing for many years, high-strength no-shrinkage grouting material has used widely in rebuilding and strengthening engineering of concrete structure and railway and bridge engineering, besides secondly grouting of equipment basement. Key words: building material; grouting material; standard;application 水泥基灌浆料与传统的细石混凝土相比，具有流动性更好、强度更高和施工易于控制的特点；与传统的环氧砂浆相比，具有膨胀性好，施工简便快捷等特点。自20世纪90年代初，我国自主研发生产的水泥基灌浆材料在众多大中型企业的设备安装、建筑结构加固改造工程中得到广泛应用。 目前国内从事水泥基灌浆材料的生产企业达200余家，年产量近50万t。近年来,由于新材料发展日新月异，新的外加剂如雨后春笋，我国灌浆料的技术性能提高，其各项技术性能已达到国际水平。灌浆料的使用，已从并获得了良好的效果。GB/T50448-2008），系统地对灌浆工程的设计、施工、质量控制与工程验收提出了具体要求。 1.2 灌浆料性能指标的发展 灌浆料产品性能近年来发展很快，尤其是流动度等各项指标。以上海宝冶工程技术有限公司生产的BY系列灌浆料为例，在20世纪90年代其流动度指标指标一直沿袭日本“塔斯库”的方法，用“s”来计量。后来随着国内相关规范及标准的出台，统一使用“mm”作为流动度的计量单位，用行星式水泥胶砂搅拌机和截锥圆模（下口内径（100±0.5）mm,上口内径（70±0.5）mm，高（60±0.5）mm）等仪器。BY系列灌浆料的主要性能指标如表1所示。 随着冬期施工工艺的发展，对用于冬期施工的灌浆料性能指标也提出了明确要求，如表2所示。 表2中，R-7表示负温养护7d试件抗压强度与标准养护28d试件抗压强度的比值；R-7+28、R-7+56分别表示负温养护7d转标准养护28d和负温养护7d转标准养护56d试件抗压强度与标准养护28d试件抗压强度的比值。 用于高温环境的灌浆料性能在温度为200、300、400、500℃时，抗压强度比≥100%。20次热震性：①试块表面无脱落；②热震后的试件浸水端（或整块试块）抗压强度与试件标准养护28d的抗压强度比≥90%。 表1 BY系列灌浆料主要性能指标 Table 1 Main performance indexes of BY-type guouting material 性能 BY-40 BY-60 BY-80 BY-20H2 抗压强度 （≥）/MPa 1d 22 30 30 30；(2h,20) 3d 40 50 55 45 28d 60