Sb含量对Sn-Bi系焊料性能的影响.pdfVIP

Availableonlineat、^n^n^，．sciencedirect．com 秽 Transactionsof 酶 ScienceDirect NonferrousM etals 蠹 SocietyofChina Press Trans．NonferrousMet．Soc．China24(2014)184—191 ww w ．tnm sc．cn EffectofSbcontentonpropertiesofSn—。—Bisolders ChengZHANG，Si．dongLIU ，Guo—tongQIAN ，JianZHOU ，FengXUE 1．SchoolofMaterialsScienceandEngineering，SoutheastUniversity,Nanjing211189，China； 2．ShaoxingTianlongTinMaterialsCo．，Ltd．，Shaoxing312001，China Received19December2012；accepted15July2013 Abstract：TheefrectofSbcontentonthepropertiesofSn—Bisolderswasstudied．Thenonequilibrium meltingbehaviorsofaseries ofSn-Bi-Sbsolderswereexaminedbvdiffrentialscanningcalorimetry(DSC)．Thespreadingtestwascarriedouttocharacterize thewettabilityOfSn—Bi-SbsoldersonCusubstrate．Themechanicalpropertiesofthesolders／Cuiointswereevaluated．Theresults show thattheternary alloysolderscontaineutecticstructureresultingfrom quasi—periteticreaction．WiththeincreaseofSbcontent． theamountoftheeutecticsturctureincreases．Ataheatingrateof5。C／min，Sn-Bi-Sballoysexhibitahighermeltingpointanda widermeltingrange．A smallamountofSbhasan impactonthewettabilityofSn-Bisolders．Thereaction layersforillduring spreadingprocess．Sbisdetectedinthereaction1ayerwhileBiisnotdetected．Thetota1thicknessofreactionlayerbetweensolder and Cuincreaseswim theincreaseoftheSb content．TheshearstrengthoftheSn-Bi-Sb soldersincreasesastheSb content lncreases． Kevwords：lead—rfeesolder；Sn