N含量对07MnNiMoVDR调质钢性能及影响与研究.pdfVIP

N 含量对 07MnNiMoVDR 调质钢的性能影响研究 杨小军 袁 源 刘永龙 （湖南华菱湘钢科技开发中心，湘潭 411101 ） 1 摘 要 本文利用光谱对湘钢生产的 07MnNiMoVDR 调质钢进行了成分分析，利用 JSM6490-LV 扫描电镜和 EDS 能谱仪对试样进行金相组织分析和夹杂物分析， 并利用 MMS-200 热模拟试验机对不同强度的试验钢进行了连续 冷却相变研究。结果显示 N 含量对 07MnNiMoVDR 调质钢强度有显著影响，并探讨了 N 含量对强度等性能影响的 作用机理。 关键词 07MnNiMoVDR N 含量 连续冷却相变 Effect on N Content on Mechnical Property of 07MnNiMoVDR Quenched and Tempered Steel Yang Xiaojun Yuan Yuan Liu Yonglong (Hunan Valin Xiangsteel Science and Technology Development Center,Xiangtan, 411101) Abstract In this paper, chemical composition of the 07MnNiMoVDR quenched and tempered steel were analysised. The microstructure and the inclusion of the plates were observed by using JSM-6490LV SEM and EDS. The continuous cooling transformation characters of the experiment steel were studied by using MMS-200 thermal simulation test machine. The results showed that N content of 07MnNiMoVDR hade a significant effect on the strength of the experiment steel. The mechanism of N content on mechanical properties were also disscussed in this paper. Key words 07MnNiMoVDR, N content, continuous cooling transformation 1 引言 以07MnNiMoVDR 为代表的用于压力容器、工程机械制造等领域的高强度板材，不仅要求足够的强度, 还要求具有良好的塑韧性及低的韧脆转变温度和焊接性能，因此该类钢材必须具有较低的合金元素含量，尤 其是碳含量。利用适当的 TMCP 和调质工艺生产时，微量硼与铌钒等合金元素共同作用能够强烈地抑制γ →α转变[1]，获得由针状铁素体、低碳贝氏体、回火索氏体等组成的多相组织，从而获得综合性能优异的钢 材。在降低钢中碳、锰等合金元素含量的同时加入了微量的硼，可平衡钢板强度、塑性、韧脆转变温度间的 关系，是目前最经济有效的合金设计方法。然而微合金钢中固溶 B 的收得率波动会影响到此类高强钢的性 能稳定[2] 。本文对湘钢生产的 07MnNiMoVDR 调质钢进行显微组织分析和成分分析，探讨了 N 含量对强度 等性能影响的作用机理。 2 实验材料和方法 实验所取试样来自湘钢正常生产过程中的 07MnNiMoVDR 调质钢。所取的两批试样分别来自两块典型 杨小军，男，工程师，wuthering_h@126.com 8-666 第八届（2011 ）中国钢铁年会论文集 强度批号。两批试样的力学性能和化学成分对比分别见表 1 和表 2 。金相和夹杂物试样分别取自板材的横截 面和纵截面。热模拟试样取自板材的 1/4 厚度位置，规格为φ8mm×15mm，热模拟实验工艺为：将试样以10 ℃/s的速度升温到920℃，保温300s，再