MSA 镀锡研究进展 刘丽愉，安成强，林雪 沈阳理工大学 环境与化学工程学院，辽宁 沈阳 110159 摘 要：甲基磺酸（MSA ）体系电解液在环保方面具有明显优势,越来越多以MSA 替代现有电解 液方面的研究；市场上部分钢板镀锡工艺也转向采用甲基磺酸镀锡电解液。本文主要介绍了甲基 磺酸盐镀锡的国内外的发展状况以及 MSA 镀锡工艺的优点、种类和工艺规范，展望了甲基磺酸 盐镀锡的发展前景。 关键词：甲基磺酸；电镀锡；镀锡种类；镀层性能 MSA Tin Research Progress Liu Liyu，An Chengqiang，Lin Xue School of Environmental and Chemical Engineering; Shenyang Ligong University ， Liaoning ，Shenyang ，110159 Abstract: The electrolyte of methyl sulfonic acid (MSA) system has some significant advantages on the environmental protection, so it increasingly replaced the existing electrolyte research.In addition, parts of steel tin process on the market also turned to use methyl sulfonic acid tinplating electrolyte. This article mainly introduced the methyl sulfonic acid salt tin of domestic and foreign development status and MSA tin plating technology advantages of types and process specification. At last, researches on methyl sulfonic acid salt tinplating development have also been prospected. Keywords: tmethanesulfonic acid; tinplating; tin kinds; technological conditions 1 引言 电镀纯锡工艺由于镀层成分单一，与各种无铅焊料易于匹配，使用范围广, 且镀液简单，便 [1,2] 于维护和管理，成本也较低，在电子行业中得到普遍认可 。甲磺酸镀锡体系以其镀液稳定， 电流效率高，工作电流密度大，镀层沉积速度快，质量高，镀液无氟污染，毒性小，极易生物降 解，对设备的腐蚀性小，Sn2+ 的氧化程度低且可以获得光亮镀层等优点，成为目前研究的热点, 是应用最广的镀锡体系之一。高速电镀可以减少生产设备和时间，提高生产效率，降低成本，因 [3~9] 此，该领域的研究国内一直以来十分关注 。 2 MSA 镀锡国内外的发展现状 镀锡的研究已经有很多年的历史，早在1810年，国外就开始使用热浸镀锡板制造食品储藏容 [ 10] 器,而镀锡钢板的生产则始于1917年 ，但以甲烷磺酸为主的烷基磺酸用于电镀的研究最早是在 1940年,但直至1980年才开始在工业上应用[ 11 ] 。在过去的几十年中，国外尤其是美国对MSA高 速电镀锡的研究较多也较全面，取得了一定的进展。目前，虽然甲基磺酸盐镀锡工艺已经成熟， 以美国为首的发达国家已经应用于生产，我国也在上世纪80 年代末90 年代初才开始引进国外工 艺并投入生产，但对镀锡液