耐腐蚀和电化学行为的电镀镍钴铁合金.docVIP

耐腐蚀和电化学行为的电镀镍钴合金?Corrosion resistance and electrodeposition behavior of electrodeposited nickel-cobalt-iron alloys? 本文的目的是调查的电镀铁镍钴合金的耐腐蚀性和电行为。此外，到钢基体的酸性硫酸浴三元铁镍钴合金的电相比，钴??，铁镀层的特点。?- 设计/方法/方式 - 电调查，开展了利用循环伏安和恒流技术，而电位极化电阻和阳极线性扫描伏安法技术用于腐蚀研究。通过X射线衍射分析相结构进行了表征。表面形貌和化学组成的存款，利用扫描电子显微镜和原子吸收光谱仪，分别进行了检查。?- 结果 - 得到的结果显示，镍钴铁合金铁，（Fe1.8Ni）和（FECO）相混合组成。结果发现，得到的镍钴合金具有更可取的表面外观和更好的耐腐蚀性比较Co-Fe合金中，在类似条件下的电。?- 实际意义 - 成功电镀镍钴合金，硫酸浴。这种合金有限公司铁矿床比较表明较高的防腐。镍钴合金，可用于在行业如汽车行业。此外，它有一个特别的兴趣，由于它是能够表现出稳定的磁学性质。?- 原创/值 - 这项工作的目的是评估三元合金电镀的影响，对钢材的腐蚀。到现在为止，很少有研究报告在这方面。结果发现，镍的存在可以提高钢的耐腐蚀性。? Corrosion resistance and electrodeposition behavior of electrodeposited nickel-cobalt-iron alloys? The purpose of this paper is to investigate the corrosion resistance and the electrodeposition behavior of electrodeposited nickel-cobalt-iron alloys. Also, the electrodeposition of ternary nickel-cobalt-iron alloy from acidic sulfate bath onto a steel substrate was compared with the characteristics of Co-Fe electrodeposits. - Design/methodology/approach – The investigation of electrodeposition was carried out using cyclic voltammetry and galvanostatic techniques, while potentiodynamic polarization resistance and anodic linear sweep voltammetry techniques were used for corrosion study. The phase structure was characterized by means of X-ray diffraction analysis. Surface morphology and chemical composition of the deposits were examined by using scanning electron microscopy and atomic absorption spectroscopy, respectively. - Findings – The obtained results revealed that the Ni-Co-Fe alloys consisted of a mixture of iron, (Fe1.8Ni) and (FeCo) phases. It was found that the obtained Ni-Co-Fe alloy exhibited more preferred surface appearance and better corrosion resistance in comparison to Co-Fe alloy that electrodeposited at similar conditions. - Practical implications – Ni-Co-Fe alloy was successfully electroplated from sulfate bath. This alloy showed higher anticorrosion in comparison with Co-Fe deposits. Ni-Co-Fe alloy c