Al2O3和Y2O3改性的低温渗铬涂层的循环氧化和热腐蚀性能.pdfVIP

Trans. Nonferrous Met. Soc. China 23(2013) 2923−2928 Cyclic oxidation and hot corrosion of Al O or Y O -dispersed low-temperature chromizing coating 2 3 2 3 Hai-jun ZHANG, Jian-feng SUN, Yue-bo ZHOU College of Materials Science and Engineering, Heilongjiang Institute of Science and Technology, Harbin 150027, China Received 10 September 2012; accepted 8 January 2013 Abstract: Chromium coatings with and without Al O or Y O particles were prepared by chromizing the as-deposited Ni-film with 2 3 2 3 and without Al O or Y O particles using a conventional pack-cementation method at 800 °C. The cyclic oxidation at 800 °C and hot 2 3 2 3 corrosion in molten 75% Na SO +25% NaCl at 800 °C of the three different chromizing coatings were investigated. The effects of 2 4 Al O or Y O on the cyclic oxidation and hot corrosion behavior of the chromizing coatings were discussed. Microstructure results 2 3 2 3 show that the codeposited Al O or Y O particles significantly retard the grain growth of the chromizing coating, which increases 2 3 2 3 the cyclic oxidation and hot corrosion resistance of the chromizing coatings, due to the more rapid formation of purer and denser chromia scale. Key words: electrodeposition; chromizing coating; cyclic oxidation; hot corrosion forward but still are in dispute [9]. ZHOU et al [13,14] 1 Introduction also found that the chromizing process was main