2124铝合金的单、双曲率蠕变时效成形(英文期刊).pdfVIP

Trans. Nonferrous Met. Soc. China 23(2013) 1922−1929 Creep age forming of 2124 aluminum alloy with single/double curvature Jin ZHANG, Yun-lai DENG, Si-yu LI, Ze-yu CHEN, Xin-ming ZHANG School of Materials Science and Engineering, Central South University, Changsha 410083, China Received 25 September 20 12; accepted 19 December 2012 Abstract: In order to investigate the springback rules, the variation characteristics of physical property and microstructure in bending creep age forming process, a series of creep forming tests of 2124 aluminum alloy were conducted based on three kinds of single and double curvature forming tools. The results show that the spingback rate would be the minimum under the optimal coupling conditions among the temperature, aging time and internal stress state of material. Difference exists in the two directions of the formed sample with double curvature, but the curvature variation keeps the same. Yield strength, ultimate tensile strength and fracture toughness of the double curvature formed sample appear to be higher than those of the single curvature formed sample under the same aging condition, but the elongation and the anisotropy are opposite. Key words: springback; creep age forming; double curvature bending; 2124 aluminum alloy aluminum alloy. ARABI et al [12] investigated the 1 Introduction effects of time and temperature on the creep forming of 7075 aluminum alloy. To predict the springback, many Creep age forming (CAF), a novel process which creep consti