《Hotcompression behavior of Al1Mn1Mg alloy》.pdfVIP

J. Cent. South Univ. Technol. (2010) 17: 425−430 DOI: 10.1007/s11771−010−0501−9 Hot-compression behavior of Al-1Mn-1Mg alloy ZHANG Xin-ming(张新明), XU Min(徐敏), TANG Jian-guo(唐建国), OU Jun(欧军) School of Materials Science and Engineering, Central South University, Changsha 410083, China © Central South University Press and Springer-Verlag Berlin Heidelberg 2010 Abstract: The hot-compression of Al-1Mn-1Mg (mass fraction, %) alloy sample was carried out on a Gleeble−1500 thermo-simulator at deformation temperatures from 320 to 400 ℃ and strain rates from 0.1 to 10 s−1 by total strain of 1.4. Microstructure and texture evolution of the hot-compressed alloy were investigated by optical microscopy and X-ray diffraction analysis, respectively. The results show that the relationship among flow stress σ, deformation temperature T and strain rate ε can be expressed in the form of ln A . The threshold value of ln Z (Z is Zener-Hollomon parameter) β σ = ln ε + Q /( RT ) − characterizing the dynamic recrystallization (DRX) is 46, below which the DRX takes place. A strong P orientation {011}〈455〉 associated with a weak cube orientation {100}〈001〉 is found in the recrystallized sample during hot-compression. Key words: Al-1Mn-1Mg alloy; hot-compression; dynamic recovery; dynamic recrystallization; texture compression behavior for guiding its manufacture 1 Introduction