《MgNdGd三元系723 K的等温截面（英文版）》.pdfVIP

Trans. Nonferrous Met. Soc. China 24(2014) 777−782 Isothermal section of Mg−Nd−Gd ternary system at 723 K Long XIAO1 1 1 1 1 1,2 3 , Yan ZHONG , Cui-ping CHEN , Ming-ming WULIU , Tian-kuang LUO , Li-bin LIU , Kui LIN 1. School of Materials Science and Engineering, Central South University, Changsha 410083, China; 2. Education Ministry Key Laboratory of Non-ferrous Materials Science and Engineering, Changsha 410083, China; 3. Guangxi Research Center of Analysis Test, Nanning 530022, China Received 20 March 2013; accepted 5 November 2013 Abstract: An isothermal section of the Mg−Nd−Gd ternary system at 723 K was established by diffusion triple technique and electron probe microanalysis (EPMA). Mg Gd and Mg Nd form a continuous solid solution (Gd,Nd) Mg, and a continuous solid 3 3 3 solution (Gd,Nd)Mg is also formed between MgGd and MgNd. Mg Gd, Mg Gd, Mg Gd, Mg Nd , (Gd,Nd) Mg and (Gd,Nd)Mg are 7 5 2 41 5 3 found in the ternary system. In these intermetallic phases, Mg Gd has been reported to be a metastable phase in previous literatures. 7 The solubilities of Mg, Gd and Nd in all the phases were detected. Furthermore, four three-phase equilibria, α(Mg)+Mg Gd+